Steel P355GH vs P355NL2
Steel · grade comparison
Steel P355GH and P355NL2 are both steel grades. Both yield at about 385 MPa — strength does not separate them. P355GH is harder — 165 HB against 155 HB for P355NL2 — which matters for wear surfaces and threads. P355NL2 conducts electricity better (10.5 % IACS vs 8.2 % IACS). On the shop floor, P355NL2 sits in a lower cost tier (budget, $) than P355GH (standard, $$).
P355GHChoose it when surface hardness matters.
P355NL2Choose it when cost is the deciding factor.
P355GH vs P355NL2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Tensile Strength (Ultimate) 550 MPa79.8 ksi · Yield Strength (0.2% offset) 385 MPa55.8 ksi · Compressive Strength 385 MPa55.8 ksi · Shear Strength 340 MPa49.3 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Thermal Diffusivity
Same in both: Specific Strength (UTS / density) 70 kN·m/kg · Specific Stiffness (E / density) 26.8 MN·m/kg · Modulus of Resilience 353 kJ/m³ · Thermal Shock Resistance Index 10
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | P355GH | P355NL2 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
P355GH vs P355NL2 — frequently asked
What is the difference between P355GH and P355NL2?
Steel P355GH and P355NL2 are both steel grades. Both yield at about 385 MPa — strength does not separate them. P355GH is harder — 165 HB against 155 HB for P355NL2 — which matters for wear surfaces and threads.
Which is cheaper, P355GH or P355NL2?
P355NL2 is the lower-cost material: it sits in the budget tier ($) while P355GH is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose P355GH over P355NL2?
Pick P355GH when surface hardness matters. Pick P355NL2 when cost is the deciding factor.
Ready to make it?
Upload a CAD file and FabDigit prices the part in P355GH and P355NL2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.