Steel GX3Ni36 vs K93050
Steel · grade comparison
Steel GX3Ni36 and K93050 are both steel grades. K93050 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 240 MPa (34.8 ksi) for GX3Ni36, about 17% more; tensile strength follows at 490 MPa (71.1 ksi) vs 450 MPa (65.3 ksi). K93050 is the more ductile: elongation 40% versus 25% for GX3Ni36. K93050 runs hotter in service (230°C vs 200°C continuous). On the shop floor, K93050 welds better (very good vs good).
K93050Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
GX3Ni36 vs K93050: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 55 GPa8 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 515 J/kg·K0.12 BTU/lb·°F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.1 % IACS · Electrical Resistivity 8.2×10⁻⁷ Ω·m32.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Machinability 30 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | GX3Ni36 | K93050 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
GX3Ni36 vs K93050 — frequently asked
Is K93050 stronger than GX3Ni36?
Yes. K93050 has a typical yield strength of 280 MPa (40.6 ksi) against 240 MPa (34.8 ksi) for GX3Ni36 — about 17% more. Tensile strength is 490 MPa (71.1 ksi) vs 450 MPa (65.3 ksi).
Which is cheaper, GX3Ni36 or K93050?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, GX3Ni36 or K93050?
K93050. Its weldability rates very good (75/100) against good (58/100) for GX3Ni36.
Ready to make it?
Upload a CAD file and FabDigit prices the part in GX3Ni36 and K93050 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.