Steel 4J32 vs GX3Ni36
Steel · grade comparison
Steel 4J32 and GX3Ni36 are both steel grades. 4J32 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 240 MPa (34.8 ksi) for GX3Ni36, about 17% more; tensile strength follows at 490 MPa (71.1 ksi) vs 450 MPa (65.3 ksi). 4J32 is the more ductile: elongation 35% versus 25% for GX3Ni36, and 4J32 is harder (140 HB vs 130 HB). On the shop floor, 4J32 welds better (very good vs good).
4J32Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
4J32 vs GX3Ni36: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Same in both: Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Thermal Conductivity 11 W/m·K6.4 BTU/hr·ft·°F · Specific Heat Capacity 515 J/kg·K0.12 BTU/lb·°F · Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 2.6 mm²/s
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4J32 | GX3Ni36 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
4J32 vs GX3Ni36 — frequently asked
Is 4J32 stronger than GX3Ni36?
Yes. 4J32 has a typical yield strength of 280 MPa (40.6 ksi) against 240 MPa (34.8 ksi) for GX3Ni36 — about 17% more. Tensile strength is 490 MPa (71.1 ksi) vs 450 MPa (65.3 ksi).
Which is cheaper, 4J32 or GX3Ni36?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, 4J32 or GX3Ni36?
4J32. Its weldability rates very good (70/100) against good (58/100) for GX3Ni36.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4J32 and GX3Ni36 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.