Steel Ferrium M54 vs H11
Steel · grade comparison
Steel Ferrium M54 and H11 are both steel grades. Ferrium M54 is the stronger of the two: yield strength 1,725 MPa (250 ksi) against 510 MPa (74 ksi) for H11, about 3.4 times as much; tensile strength follows at 2,020 MPa (293 ksi) vs 800 MPa (116 ksi). In exchange, H11 is the more ductile: elongation 20% versus 12% for Ferrium M54, and Ferrium M54 is harder (600 HV vs 210 HV). H11 runs hotter in service (540°C vs 400°C continuous) and H11 conducts heat better (25 W/m·K vs 22 W/m·K). On the shop floor, H11 machines more easily (good vs poor) and H11 sits in a lower cost tier (standard, $$) than Ferrium M54 (high, $$$$).
Ferrium M54Choose it when strength drives the design.
H11Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Ferrium M54 vs H11: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Hardness, Brinell
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Latent Heat of Fusion
Electrical
Conductivity and insulation.
Electrical Resistivity
Electrical Conductivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Castability
Brazeability / Solderability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Ferrium M54 | H11 |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$$$ High | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
Ferrium M54 vs H11 — frequently asked
Is Ferrium M54 stronger than H11?
Yes. Ferrium M54 has a typical yield strength of 1,725 MPa (250 ksi) against 510 MPa (74 ksi) for H11 — about 3.4 times as much. Tensile strength is 2,020 MPa (293 ksi) vs 800 MPa (116 ksi).
Which is cheaper, Ferrium M54 or H11?
H11 is the lower-cost material: it sits in the standard tier ($$) while Ferrium M54 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Ferrium M54 or H11?
H11. Its machinability rates good (55/100) against poor (22/100) for Ferrium M54; for welding the order is H11 first (fair, 35/100) then Ferrium M54 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ferrium M54 and H11 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.