Steel ER70S-2 vs ER70S-B2L
Steel · grade comparison
Steel ER70S-2 and ER70S-B2L are both steel grades. ER70S-B2L is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 450 MPa (65.3 ksi) for ER70S-2, about 16% more; tensile strength follows at 620 MPa (89.9 ksi) vs 560 MPa (81.2 ksi). In exchange, ER70S-2 is the more ductile: elongation 28% versus 22% for ER70S-B2L, and ER70S-B2L is harder (205 HB vs 155 HB). ER70S-B2L runs hotter in service (450°C vs 400°C continuous) and ER70S-2 conducts heat better (48 W/m·K vs 42 W/m·K). On the shop floor, ER70S-2 machines more easily (good vs fair), ER70S-2 welds better (excellent vs very good), and ER70S-2 sits in a lower cost tier (standard, $$) than ER70S-B2L (premium, $$$).
ER70S-2Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
ER70S-B2LChoose it when strength drives the design, or when the part sees heat.
ER70S-2 vs ER70S-B2L: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg · Thermal Shock Resistance Index 10
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ER70S-2 | ER70S-B2L |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
ER70S-2 vs ER70S-B2L — frequently asked
Is ER70S-B2L stronger than ER70S-2?
Yes. ER70S-B2L has a typical yield strength of 520 MPa (75.4 ksi) against 450 MPa (65.3 ksi) for ER70S-2 — about 16% more. Tensile strength is 620 MPa (89.9 ksi) vs 560 MPa (81.2 ksi).
Which is cheaper, ER70S-2 or ER70S-B2L?
ER70S-2 is the lower-cost material: it sits in the standard tier ($$) while ER70S-B2L is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, ER70S-2 or ER70S-B2L?
ER70S-2. Its machinability rates good (62/100) against fair (50/100) for ER70S-B2L; for welding the order is ER70S-2 first (excellent, 98/100) then ER70S-B2L (very good, 75/100).