Steel E80C-Ni2 vs ER70S-2
Steel · grade comparison
Steel E80C-Ni2 and ER70S-2 are both steel grades. E80C-Ni2 is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 450 MPa (65.3 ksi) for ER70S-2, about 16% more; tensile strength follows at 620 MPa (89.9 ksi) vs 560 MPa (81.2 ksi). E80C-Ni2 is harder — 190 HB against 155 HB for ER70S-2 — which matters for wear surfaces and threads. ER70S-2 conducts heat better (48 W/m·K vs 40 W/m·K). On the shop floor, ER70S-2 welds better (98 vs 88 out of 100) and ER70S-2 sits in a lower cost tier (standard, $$) than E80C-Ni2 (premium, $$$).
E80C-Ni2Choose it when strength drives the design, or when surface hardness matters.
ER70S-2Choose it when it will be welded, or when cost is the deciding factor.
E80C-Ni2 vs ER70S-2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.5 µm/m·K6.9 µin/in·°F · Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Formability (cold)
Brazeability / Solderability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg · Thermal Shock Resistance Index 10
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | E80C-Ni2 | ER70S-2 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
E80C-Ni2 vs ER70S-2 — frequently asked
Is E80C-Ni2 stronger than ER70S-2?
Yes. E80C-Ni2 has a typical yield strength of 520 MPa (75.4 ksi) against 450 MPa (65.3 ksi) for ER70S-2 — about 16% more. Tensile strength is 620 MPa (89.9 ksi) vs 560 MPa (81.2 ksi).
Which is cheaper, E80C-Ni2 or ER70S-2?
ER70S-2 is the lower-cost material: it sits in the standard tier ($$) while E80C-Ni2 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, E80C-Ni2 or ER70S-2?
ER70S-2, by a small margin. Both rate good for machinability — 62/100 against 55/100 for E80C-Ni2; for welding the order is ER70S-2 first (excellent, 98/100) then E80C-Ni2 (excellent, 88/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E80C-Ni2 and ER70S-2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.