Steel CPM 10V Annealed vs CPM 10V H&T 62-64 HRC
Steel · CPM 10V temper comparison
CPM 10V Annealed and CPM 10V H&T 62-64 HRC are two conditions of the same steel grade, CPM 10V: Annealed versus H&T 62-64 HRC (high austenitising (~1150–1175 °C) + triple temper 540 °C). The chemistry is identical, so every difference below comes from the condition. CPM 10V H&T 62-64 HRC is the stronger of the two: yield strength 1,950 MPa (283 ksi) against 560 MPa (81.2 ksi) for CPM 10V Annealed, about 3.5 times as much; tensile strength follows at 2,100 MPa (305 ksi) vs 830 MPa (120 ksi). In exchange, CPM 10V Annealed is the more ductile: elongation 12% versus 1% for CPM 10V H&T 62-64 HRC, and CPM 10V H&T 62-64 HRC is harder (690 HB vs 255 HB). On the shop floor, CPM 10V Annealed machines more easily (poor vs not recommended) and CPM 10V Annealed welds better (poor vs not recommended).
CPM 10V AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
CPM 10V H&T 62-64 HRCChoose it when strength drives the design.
CPM 10V Annealed vs CPM 10V H&T 62-64 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
CPM 10V AnnealedCPM 10V H&T 62-64 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 88 GPa12.8 Msi · Bulk Modulus 170 GPa24.7 Msi · Poisson's Ratio 0.3 · Reduction in Area 22% · Hardness, Rockwell B 101 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.41 g/cm³0.27 lb/in³ · Melting Point (Solidus) 1,280°C2,336 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.6 µm/m·K5.9 µin/in·°F · Min Service Temperature -70°C-94 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 35 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 75 MJ/kg32,244 BTU/lb · Embodied Carbon (primary production) 5.5 kg CO₂/kg · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CPM 10V Annealed vs CPM 10V H&T 62-64 HRC — frequently asked
Is CPM 10V H&T 62-64 HRC stronger than CPM 10V Annealed?
Yes. CPM 10V H&T 62-64 HRC has a typical yield strength of 1,950 MPa (283 ksi) against 560 MPa (81.2 ksi) for CPM 10V Annealed — about 3.5 times as much. Tensile strength is 2,100 MPa (305 ksi) vs 830 MPa (120 ksi).
Which condition does FabDigit quote by default, Annealed or H&T 62-64 HRC?
Annealed is the default CPM 10V condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, CPM 10V Annealed or CPM 10V H&T 62-64 HRC?
CPM 10V Annealed. Its machinability rates poor (25/100) against not recommended (4/100) for CPM 10V H&T 62-64 HRC; for welding the order is CPM 10V Annealed first (poor, 15/100) then CPM 10V H&T 62-64 HRC (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in CPM 10V Annealed and CPM 10V H&T 62-64 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.