Steel AR500 vs NM500
Steel · grade comparison
Steel AR500 and NM500 are both steel grades, both wear resistant steel. Both yield at about 1,350 MPa — strength does not separate them. AR500 is the more ductile: elongation 9% versus 8% for NM500. AR500 conducts heat better (40 W/m·K vs 34 W/m·K). On the shop floor, AR500 welds better (45 vs 35 out of 100) and NM500 sits in a lower cost tier (standard, $$) than AR500 (high, $$$$).
AR500Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
NM500Choose it when cost is the deciding factor.
AR500 vs NM500: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Fatigue Strength (Endurance Limit) 700 MPa102 ksi · Hardness, Brinell 500 HB · Hardness, Rockwell C 50 HRC · Hardness, Vickers 525 HV
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Max Service Temperature (continuous) 250°C482 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Machinability 12 / 100 · Formability (cold) 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Same in both: Embodied Carbon (primary production) 2.3 kg CO₂/kg · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AR500 | NM500 |
|---|---|---|
| Default condition | Q&T | Q&T |
| Relative cost | $$$$ High | $$ Standard |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
AR500 vs NM500 — frequently asked
What is the difference between AR500 and NM500?
Steel AR500 and NM500 are both steel grades, both wear resistant steel. Both yield at about 1,350 MPa — strength does not separate them. AR500 is the more ductile: elongation 9% versus 8% for NM500.
Which is cheaper, AR500 or NM500?
NM500 is the lower-cost material: it sits in the standard tier ($$) while AR500 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, AR500 or NM500?
AR500. Its weldability rates fair (45/100) against fair (35/100) for NM500.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AR500 and NM500 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.