Steel A897 Grade 3 vs G3500
Steel · grade comparison
Steel A897 Grade 3 and G3500 are both steel grades. A897 Grade 3 is the stronger of the two: yield strength 810 MPa (117 ksi) against 180 MPa (26.1 ksi) for G3500, about 4.5 times as much; tensile strength follows at 1,120 MPa (162 ksi) vs 250 MPa (36.3 ksi). A897 Grade 3 is the more ductile: elongation 8% versus 0.5% for G3500, and A897 Grade 3 is harder (340 HB vs 225 HB). A897 Grade 3 is stiffer (168 GPa vs 110 GPa) and G3500 runs hotter in service (400°C vs 300°C continuous). On the shop floor, G3500 machines more easily (very good vs poor), G3500 welds better (poor vs not recommended), and G3500 sits in a lower cost tier (budget, $) than A897 Grade 3 (standard, $$).
A897 Grade 3Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
G3500Choose it when the part sees heat, or when the part is machined in volume.
A897 Grade 3 vs G3500: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,150°C2,102 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 220 J/g94.6 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 30 L/kg3.6 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A897 Grade 3 | G3500 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A897 Grade 3 vs G3500 — frequently asked
Is A897 Grade 3 stronger than G3500?
Yes. A897 Grade 3 has a typical yield strength of 810 MPa (117 ksi) against 180 MPa (26.1 ksi) for G3500 — about 4.5 times as much. Tensile strength is 1,120 MPa (162 ksi) vs 250 MPa (36.3 ksi).
Which is cheaper, A897 Grade 3 or G3500?
G3500 is the lower-cost material: it sits in the budget tier ($) while A897 Grade 3 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A897 Grade 3 or G3500?
G3500. Its machinability rates very good (78/100) against poor (25/100) for A897 Grade 3; for welding the order is G3500 first (poor, 25/100) then A897 Grade 3 (not recommended, 12/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A897 Grade 3 and G3500 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.