Steel A182 F5a vs AR400
Steel · grade comparison
Steel A182 F5a and AR400 are both steel grades. AR400 is the stronger of the two: yield strength 1,050 MPa (152 ksi) against 480 MPa (69.6 ksi) for A182 F5a, about 119% more; tensile strength follows at 1,250 MPa (181 ksi) vs 690 MPa (100 ksi). In exchange, A182 F5a is the more ductile: elongation 24% versus 11% for AR400, and AR400 is harder (400 HB vs 215 HB). A182 F5a runs hotter in service (600°C vs 250°C continuous) and AR400 conducts heat better (42 W/m·K vs 36 W/m·K). On the shop floor, A182 F5a machines more easily (fair vs poor), AR400 welds better (good vs fair), and A182 F5a sits in a lower cost tier (standard, $$) than AR400 (premium, $$$).
A182 F5aChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AR400Choose it when strength drives the design, or when it will be welded.
A182 F5a vs AR400: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Electrical Conductivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A182 F5a | AR400 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Q&T |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A182 F5a vs AR400 — frequently asked
Is AR400 stronger than A182 F5a?
Yes. AR400 has a typical yield strength of 1,050 MPa (152 ksi) against 480 MPa (69.6 ksi) for A182 F5a — about 119% more. Tensile strength is 1,250 MPa (181 ksi) vs 690 MPa (100 ksi).
Which is cheaper, A182 F5a or AR400?
A182 F5a is the lower-cost material: it sits in the standard tier ($$) while AR400 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A182 F5a or AR400?
A182 F5a. Its machinability rates fair (48/100) against poor (22/100) for AR400; for welding the order is AR400 first (good, 55/100) then A182 F5a (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A182 F5a and AR400 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.