Steel 1117 vs 1132
Steel · grade comparison
Steel 1117 and 1132 are both steel grades. 1132 is the stronger of the two: yield strength 530 MPa (76.9 ksi) against 235 MPa (34.1 ksi) for 1117, about 126% more; tensile strength follows at 620 MPa (89.9 ksi) vs 425 MPa (61.6 ksi). In exchange, 1117 is the more ductile: elongation 33% versus 12% for 1132, and 1132 is harder (183 HB vs 121 HB). On the shop floor, 1117 welds better (fair vs poor).
1117Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
1132Choose it when strength drives the design.
1117 vs 1132: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Castability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1117 | 1132 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | HR | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
1117 vs 1132 — frequently asked
Is 1132 stronger than 1117?
Yes. 1132 has a typical yield strength of 530 MPa (76.9 ksi) against 235 MPa (34.1 ksi) for 1117 — about 126% more. Tensile strength is 620 MPa (89.9 ksi) vs 425 MPa (61.6 ksi).
Which is cheaper, 1117 or 1132?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1117 or 1132?
1132, by a small margin. Both rate very good for machinability — 78/100 against 70/100 for 1117; for welding the order is 1117 first (fair, 50/100) then 1132 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1117 and 1132 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.