Steel 1030 vs C45
Steel · grade comparison
Steel 1030 and C45 are both steel grades, both medium carbon steel. C45 is the stronger of the two: yield strength 400 MPa (58 ksi) against 260 MPa (37.7 ksi) for 1030, about 54% more; tensile strength follows at 650 MPa (94.3 ksi) vs 470 MPa (68.2 ksi). In exchange, 1030 is the more ductile: elongation 20% versus 17% for C45, and C45 is harder (190 HB vs 137 HB). On the shop floor, 1030 welds better (good vs fair).
1030Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C45Choose it when strength drives the design.
1030 vs C45: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 55 / 100 · Castability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1030 | C45 |
|---|---|---|
| Default condition | HR | Normalized |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
1030 vs C45 — frequently asked
Is C45 stronger than 1030?
Yes. C45 has a typical yield strength of 400 MPa (58 ksi) against 260 MPa (37.7 ksi) for 1030 — about 54% more. Tensile strength is 650 MPa (94.3 ksi) vs 470 MPa (68.2 ksi).
Which is cheaper, 1030 or C45?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, 1030 or C45?
1030. Its weldability rates good (62/100) against fair (45/100) for C45.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1030 and C45 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.