Stainless Steel 416Se Annealed vs 416Se Cold Drawn
Stainless Steel · 416Se temper comparison
416Se Annealed and 416Se Cold Drawn are two conditions of the same stainless steel grade, 416Se: Annealed versus Cold Drawn. The chemistry is identical, so every difference below comes from the condition. 416Se Cold Drawn is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 280 MPa (40.6 ksi) for 416Se Annealed, about 96% more; tensile strength follows at 655 MPa (95 ksi) vs 520 MPa (75.4 ksi). In exchange, 416Se Annealed is the more ductile: elongation 28% versus 15% for 416Se Cold Drawn, and 416Se Cold Drawn is harder (210 HB vs 160 HB). 416Se Annealed runs hotter in service (675°C vs 400°C continuous).
416Se AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
416Se Cold DrawnChoose it when strength drives the design.
416Se Annealed vs 416Se Cold Drawn: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
416Se Annealed416Se Cold Drawn
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.9 µm/m·K5.5 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.7×10⁻⁷ Ω·m22.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V · Corrosion Resistance 32 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 85% · Brazeability / Solderability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
416Se Annealed vs 416Se Cold Drawn — frequently asked
Is 416Se Cold Drawn stronger than 416Se Annealed?
Yes. 416Se Cold Drawn has a typical yield strength of 550 MPa (79.8 ksi) against 280 MPa (40.6 ksi) for 416Se Annealed — about 96% more. Tensile strength is 655 MPa (95 ksi) vs 520 MPa (75.4 ksi).
Which condition does FabDigit quote by default, Annealed or Cold Drawn?
Annealed is the default 416Se condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 416Se Annealed over 416Se Cold Drawn?
Pick 416Se Annealed when the part is bent, formed or impact-loaded, or when the part sees heat. Pick 416Se Cold Drawn when strength drives the design.
Ready to make it?