Stainless Steel 416 vs F6b
Stainless Steel · grade comparison
Stainless Steel 416 and F6b are both stainless steel grades. F6b is the stronger of the two: yield strength 660 MPa (95.7 ksi) against 275 MPa (39.9 ksi) for 416, about 140% more; tensile strength follows at 810 MPa (117 ksi) vs 515 MPa (74.7 ksi). In exchange, 416 is the more ductile: elongation 30% versus 20% for F6b, and F6b is harder (265 HB vs 155 HB). 416 runs hotter in service (650°C vs 480°C continuous). On the shop floor, 416 machines more easily (very good vs fair) and F6b welds better (fair vs poor).
416Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
F6bChoose it when strength drives the design, or when it will be welded.
416 vs F6b: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.9 µm/m·K5.5 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.7×10⁻⁷ Ω·m22.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 7 mm²/s
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 416 | F6b |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
416 vs F6b — frequently asked
Is F6b stronger than 416?
Yes. F6b has a typical yield strength of 660 MPa (95.7 ksi) against 275 MPa (39.9 ksi) for 416 — about 140% more. Tensile strength is 810 MPa (117 ksi) vs 515 MPa (74.7 ksi).
Which is cheaper, 416 or F6b?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 416 or F6b?
416. Its machinability rates very good (80/100) against fair (42/100) for F6b; for welding the order is F6b first (fair, 35/100) then 416 (poor, 22/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 416 and F6b side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.