Stainless Steel 410 vs 440A
Stainless Steel · grade comparison
Stainless Steel 410 and 440A are both stainless steel grades, both high strength ss. 440A is the stronger of the two: yield strength 415 MPa (60.2 ksi) against 310 MPa (45 ksi) for 410, about 34% more; tensile strength follows at 725 MPa (105 ksi) vs 517 MPa (75 ksi). In exchange, 410 is the more ductile: elongation 25% versus 20% for 440A, and 440A is harder (195 HB vs 155 HB). 440A runs hotter in service (760°C vs 650°C continuous). On the shop floor, 410 machines more easily (good vs fair), 410 welds better (fair vs poor), and 410 sits in a lower cost tier (premium, $$$) than 440A (high, $$$$).
410Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
440AChoose it when strength drives the design, or when the part sees heat.
410 vs 440A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 130 L/kg15.6 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26 MN·m/kg
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 410 | 440A |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | Annealed | Annealed |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 32 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, CrN, DLC, Electroless Nickel (EN), Electropolishing and 20 more.
410 vs 440A — frequently asked
Is 440A stronger than 410?
Yes. 440A has a typical yield strength of 415 MPa (60.2 ksi) against 310 MPa (45 ksi) for 410 — about 34% more. Tensile strength is 725 MPa (105 ksi) vs 517 MPa (75 ksi).
Which is cheaper, 410 or 440A?
410 is the lower-cost material: it sits in the premium tier ($$$) while 440A is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 410 or 440A?
410. Its machinability rates good (55/100) against fair (40/100) for 440A; for welding the order is 410 first (fair, 45/100) then 440A (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 410 and 440A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.