Stainless Steel 316 vs Nitronic 50
Stainless Steel · grade comparison
Stainless Steel 316 and Nitronic 50 are both stainless steel grades, both corrosion resistant ss. Nitronic 50 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 290 MPa (42.1 ksi) for 316, about 55% more; tensile strength follows at 800 MPa (116 ksi) vs 580 MPa (84.1 ksi). In exchange, 316 is the more ductile: elongation 50% versus 45% for Nitronic 50, and Nitronic 50 is harder (217 HB vs 150 HB). 316 runs hotter in service (870°C vs 800°C continuous) and 316 conducts heat better (16.3 W/m·K vs 12.5 W/m·K). On the shop floor, 316 welds better (excellent vs very good) and 316 sits in a lower cost tier (premium, $$$) than Nitronic 50 (specialty, $$$$$).
316Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Nitronic 50Choose it when strength drives the design.
316 vs Nitronic 50: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 316 | Nitronic 50 |
|---|---|---|
| Casting & forging | Yes | — |
| Default condition | Solution Annealed | Solution Annealed |
| Relative cost | $$$ Premium | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 32 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, CrN, DLC, Electroless Nickel (EN), Electropolishing and 20 more.
316 vs Nitronic 50 — frequently asked
Is Nitronic 50 stronger than 316?
Yes. Nitronic 50 has a typical yield strength of 450 MPa (65.3 ksi) against 290 MPa (42.1 ksi) for 316 — about 55% more. Tensile strength is 800 MPa (116 ksi) vs 580 MPa (84.1 ksi).
Which is cheaper, 316 or Nitronic 50?
316 is the lower-cost material: it sits in the premium tier ($$$) while Nitronic 50 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 316 or Nitronic 50?
316. Its machinability rates fair (35/100) against poor (28/100) for Nitronic 50; for welding the order is 316 first (excellent, 88/100) then Nitronic 50 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 316 and Nitronic 50 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.