Stainless Steel 1.4005 vs 410
Stainless Steel · grade comparison
Stainless Steel 1.4005 and 410 are both stainless steel grades. 1.4005 is the stronger of the two: tensile strength 550 MPa (79.8 ksi) against 517 MPa (75 ksi) for 410, about 6% more. 1.4005 is harder — 175 HB against 155 HB for 410 — which matters for wear surfaces and threads. 1.4005 is stiffer (215 GPa vs 200 GPa) and 1.4005 conducts heat better (30 W/m·K vs 24.9 W/m·K). On the shop floor, 1.4005 machines more easily (excellent vs good), 410 welds better (fair vs poor), and 410 forms better (good vs poor).
1.4005Choose it when strength drives the design, or when surface hardness matters.
410Choose it when it will be welded.
1.4005 vs 410: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 25%
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 60%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 7
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4005 | 410 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4005 vs 410 — frequently asked
Is 1.4005 stronger than 410?
Yes. 1.4005 has a typical tensile strength of 550 MPa (79.8 ksi) against 517 MPa (75 ksi) for 410 — about 6% more.
Which is cheaper, 1.4005 or 410?
1.4005 is the lower-cost material: it sits in the standard tier ($$) while 410 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4005 or 410?
1.4005. Its machinability rates excellent (85/100) against good (55/100) for 410; for welding the order is 410 first (fair, 45/100) then 1.4005 (poor, 15/100).