Precious Metal Pt70Rh30/Pt94Rh6 vs Pt90Rh10
Precious Metal · grade comparison
Precious Metal Pt70Rh30/Pt94Rh6 and Pt90Rh10 are both precious metal grades. Pt70Rh30/Pt94Rh6 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 170 MPa (24.7 ksi) for Pt90Rh10, about 47% more; tensile strength follows at 550 MPa (79.8 ksi) vs 320 MPa (46.4 ksi). In exchange, Pt90Rh10 is the more ductile: elongation 35% versus 28% for Pt70Rh30/Pt94Rh6, and Pt70Rh30/Pt94Rh6 is harder (125 HV vs 90 HV). Pt70Rh30/Pt94Rh6 is lighter (17.6 g/cm³ vs 19.97 g/cm³ for Pt90Rh10) and Pt70Rh30/Pt94Rh6 is stiffer (225 GPa vs 193 GPa). On the shop floor, Pt70Rh30/Pt94Rh6 welds better (excellent vs very good).
Pt70Rh30/Pt94Rh6Choose it when strength drives the design, or when weight is the constraint.
Pt90Rh10Choose it when the part is bent, formed or impact-loaded.
Pt70Rh30/Pt94Rh6 vs Pt90Rh10: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Vickers
Hardness, Brinell
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9.1 % IACS · Electrical Resistivity 1.9×10⁻⁷ Ω·m7.48 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Castability 45 / 100 · Brazeability / Solderability 60 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Pt70Rh30/Pt94Rh6 | Pt90Rh10 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Pt70Rh30/Pt94Rh6 vs Pt90Rh10 — frequently asked
Is Pt70Rh30/Pt94Rh6 stronger than Pt90Rh10?
Yes. Pt70Rh30/Pt94Rh6 has a typical yield strength of 250 MPa (36.3 ksi) against 170 MPa (24.7 ksi) for Pt90Rh10 — about 47% more. Tensile strength is 550 MPa (79.8 ksi) vs 320 MPa (46.4 ksi).
Which is cheaper, Pt70Rh30/Pt94Rh6 or Pt90Rh10?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, Pt70Rh30/Pt94Rh6 or Pt90Rh10?
Pt70Rh30/Pt94Rh6. Its weldability rates excellent (85/100) against very good (75/100) for Pt90Rh10.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pt70Rh30/Pt94Rh6 and Pt90Rh10 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.