Precious Metal BAg-18 vs BAg-27
Precious Metal · grade comparison
Precious Metal BAg-18 and BAg-27 are both precious metal grades. BAg-27 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 210 MPa (30.5 ksi) for BAg-18, about 19% more; tensile strength follows at 400 MPa (58 ksi) vs 380 MPa (55.1 ksi). In exchange, BAg-18 is the more ductile: elongation 28% versus 25% for BAg-27, and BAg-18 is harder (95 HB vs 90 HB). BAg-27 is lighter (9 g/cm³ vs 9.9 g/cm³ for BAg-18) and BAg-27 conducts electricity better (19 % IACS vs 17 % IACS). On the shop floor, BAg-27 machines more easily (45 vs 35 out of 100).
BAg-18Choose it when the part is bent, formed or impact-loaded.
BAg-27Choose it when strength drives the design, or when weight is the constraint.
BAg-18 vs BAg-27: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Vickers
Bulk Modulus
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 85 GPa12.3 Msi · Shear Modulus 32 GPa4.6 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Latent Heat of Fusion
Same in both: Thermal Conductivity 75 W/m·K43.3 BTU/hr·ft·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Polishability
Same in both: Weldability 20 / 100 · Castability 70 / 100 · Brazeability / Solderability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 1,500 L/kg180 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BAg-18 | BAg-27 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BAg-18 vs BAg-27 — frequently asked
Is BAg-27 stronger than BAg-18?
Yes. BAg-27 has a typical yield strength of 250 MPa (36.3 ksi) against 210 MPa (30.5 ksi) for BAg-18 — about 19% more. Tensile strength is 400 MPa (58 ksi) vs 380 MPa (55.1 ksi).
Which is cheaper, BAg-18 or BAg-27?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, BAg-18 or BAg-27?
BAg-27, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for BAg-18.
Ready to make it?
Upload a CAD file and FabDigit prices the part in BAg-18 and BAg-27 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.