Precious Metal B780 vs Silver 999
Precious Metal · grade comparison
Precious Metal B780 and Silver 999 are both precious metal grades. B780 is the stronger of the two: yield strength 125 MPa (18.1 ksi) against 55 MPa (7.98 ksi) for Silver 999, about 127% more; tensile strength follows at 310 MPa (45 ksi) vs 140 MPa (20.3 ksi). In exchange, Silver 999 is the more ductile: elongation 48% versus 30% for B780, and B780 is harder (68 HB vs 25 HB). B780 is lighter (10.05 g/cm³ vs 10.49 g/cm³ for Silver 999) and B780 is stiffer (88 GPa vs 76 GPa). On the shop floor, B780 machines more easily (50 vs 40 out of 100) and B780 sits in a lower cost tier (high, $$$$) than Silver 999 (specialty, $$$$$).
B780Choose it when strength drives the design, or when weight is the constraint.
Silver 999Choose it when the part is bent, formed or impact-loaded.
B780 vs Silver 999: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 105 J/g45.1 BTU/lb · Max Service Temperature (continuous) 250°C482 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Weldability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | B780 | Silver 999 |
|---|---|---|
| Default condition | — | O |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | — |
| Best machined surface | — | — |
B780 vs Silver 999 — frequently asked
Is B780 stronger than Silver 999?
Yes. B780 has a typical yield strength of 125 MPa (18.1 ksi) against 55 MPa (7.98 ksi) for Silver 999 — about 127% more. Tensile strength is 310 MPa (45 ksi) vs 140 MPa (20.3 ksi).
Which is cheaper, B780 or Silver 999?
B780 is the lower-cost material: it sits in the high tier ($$$$) while Silver 999 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, B780 or Silver 999?
B780, by a small margin. Both rate fair for machinability — 50/100 against 40/100 for Silver 999.
Ready to make it?
Upload a CAD file and FabDigit prices the part in B780 and Silver 999 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.