Precious Metal 85Pt-15Ir vs Silver 999
Precious Metal · grade comparison
Precious Metal 85Pt-15Ir and Silver 999 are both precious metal grades. 85Pt-15Ir is the stronger of the two: yield strength 200 MPa (29 ksi) against 55 MPa (7.98 ksi) for Silver 999, about 3.6 times as much; tensile strength follows at 480 MPa (69.6 ksi) vs 140 MPa (20.3 ksi). In exchange, Silver 999 is the more ductile: elongation 48% versus 27% for 85Pt-15Ir, and 85Pt-15Ir is harder (160 HV vs 27 HV). Silver 999 is lighter (10.49 g/cm³ vs 21.6 g/cm³ for 85Pt-15Ir) and 85Pt-15Ir is stiffer (205 GPa vs 76 GPa). On the shop floor, Silver 999 machines more easily (fair vs poor), 85Pt-15Ir welds better (very good vs good), and 85Pt-15Ir sits in a lower cost tier (high, $$$$) than Silver 999 (specialty, $$$$$).
85Pt-15IrChoose it when strength drives the design, or when the part sees heat.
Silver 999Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
85Pt-15Ir vs Silver 999: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Hardness, Brinell
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 85Pt-15Ir | Silver 999 |
|---|---|---|
| Default condition | — | O |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | — |
| Best machined surface | — | — |
85Pt-15Ir vs Silver 999 — frequently asked
Is 85Pt-15Ir stronger than Silver 999?
Yes. 85Pt-15Ir has a typical yield strength of 200 MPa (29 ksi) against 55 MPa (7.98 ksi) for Silver 999 — about 3.6 times as much. Tensile strength is 480 MPa (69.6 ksi) vs 140 MPa (20.3 ksi).
Which is cheaper, 85Pt-15Ir or Silver 999?
85Pt-15Ir is the lower-cost material: it sits in the high tier ($$$$) while Silver 999 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 85Pt-15Ir or Silver 999?
Silver 999. Its machinability rates fair (40/100) against poor (25/100) for 85Pt-15Ir; for welding the order is 85Pt-15Ir first (very good, 70/100) then Silver 999 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 85Pt-15Ir and Silver 999 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.