Precious Metal 70Ag-30Ni vs Silver 999
Precious Metal · grade comparison
Precious Metal 70Ag-30Ni and Silver 999 are both precious metal grades. 70Ag-30Ni is the stronger of the two: yield strength 110 MPa (16 ksi) against 55 MPa (7.98 ksi) for Silver 999, about 100% more; tensile strength follows at 260 MPa (37.7 ksi) vs 140 MPa (20.3 ksi). In exchange, Silver 999 is the more ductile: elongation 48% versus 25% for 70Ag-30Ni, and 70Ag-30Ni is harder (58 HB vs 25 HB). 70Ag-30Ni is lighter (9.95 g/cm³ vs 10.49 g/cm³ for Silver 999) and 70Ag-30Ni is stiffer (110 GPa vs 76 GPa). On the shop floor, 70Ag-30Ni welds better (very good vs good) and 70Ag-30Ni sits in a lower cost tier (high, $$$$) than Silver 999 (specialty, $$$$$).
70Ag-30NiChoose it when strength drives the design, or when weight is the constraint.
Silver 999Choose it when the part is bent, formed or impact-loaded.
70Ag-30Ni vs Silver 999: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 250°C482 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 70Ag-30Ni | Silver 999 |
|---|---|---|
| Default condition | — | O |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | — |
| Best machined surface | — | — |
70Ag-30Ni vs Silver 999 — frequently asked
Is 70Ag-30Ni stronger than Silver 999?
Yes. 70Ag-30Ni has a typical yield strength of 110 MPa (16 ksi) against 55 MPa (7.98 ksi) for Silver 999 — about 100% more. Tensile strength is 260 MPa (37.7 ksi) vs 140 MPa (20.3 ksi).
Which is cheaper, 70Ag-30Ni or Silver 999?
70Ag-30Ni is the lower-cost material: it sits in the high tier ($$$$) while Silver 999 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 70Ag-30Ni or Silver 999?
70Ag-30Ni, by a small margin. Both rate fair for machinability — 45/100 against 40/100 for Silver 999; for welding the order is 70Ag-30Ni first (very good, 70/100) then Silver 999 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 70Ag-30Ni and Silver 999 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.