Precious Metal B596 vs Silver 999
Precious Metal · grade comparison
Precious Metal B596 and Silver 999 are both precious metal grades. B596 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 55 MPa (7.98 ksi) for Silver 999, about 11 times as much; tensile strength follows at 760 MPa (110 ksi) vs 140 MPa (20.3 ksi). In exchange, Silver 999 is the more ductile: elongation 48% versus 3% for B596, and B596 is harder (215 HV vs 27 HV). Silver 999 is lighter (10.49 g/cm³ vs 15.5 g/cm³ for B596) and B596 is stiffer (92 GPa vs 76 GPa). On the shop floor, B596 machines more easily (good vs fair), B596 welds better (very good vs good), and B596 sits in a lower cost tier (high, $$$$) than Silver 999 (specialty, $$$$$).
B596Choose it when strength drives the design, or when the part is machined in volume.
Silver 999Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
B596 vs Silver 999: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Vickers
Reduction in Area
Hardness, Brinell
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | B596 | Silver 999 |
|---|---|---|
| Default condition | — | O |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | — |
| Best machined surface | — | — |
B596 vs Silver 999 — frequently asked
Is B596 stronger than Silver 999?
Yes. B596 has a typical yield strength of 620 MPa (89.9 ksi) against 55 MPa (7.98 ksi) for Silver 999 — about 11 times as much. Tensile strength is 760 MPa (110 ksi) vs 140 MPa (20.3 ksi).
Which is cheaper, B596 or Silver 999?
B596 is the lower-cost material: it sits in the high tier ($$$$) while Silver 999 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, B596 or Silver 999?
B596. Its machinability rates good (55/100) against fair (40/100) for Silver 999; for welding the order is B596 first (very good, 75/100) then Silver 999 (good, 60/100).