Precious Metal 18K White Gold vs 24K
Precious Metal · grade comparison
Precious Metal 18K White Gold and 24K are both precious metal grades. 18K White Gold is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 30 MPa (4.35 ksi) for 24K, about 10 times as much; tensile strength follows at 520 MPa (75.4 ksi) vs 125 MPa (18.1 ksi). In exchange, 24K is the more ductile: elongation 45% versus 35% for 18K White Gold, and 18K White Gold is harder (128 HB vs 25 HB). 18K White Gold is lighter (15.8 g/cm³ vs 19.32 g/cm³ for 24K) and 18K White Gold is stiffer (95 GPa vs 78 GPa). On the shop floor, 18K White Gold machines more easily (good vs poor) and 24K welds better (excellent vs very good).
18K White GoldChoose it when strength drives the design, or when weight is the constraint.
24KChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
18K White Gold vs 24K: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 18K White Gold | 24K |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
18K White Gold vs 24K — frequently asked
Is 18K White Gold stronger than 24K?
Yes. 18K White Gold has a typical yield strength of 300 MPa (43.5 ksi) against 30 MPa (4.35 ksi) for 24K — about 10 times as much. Tensile strength is 520 MPa (75.4 ksi) vs 125 MPa (18.1 ksi).
Which is cheaper, 18K White Gold or 24K?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 18K White Gold or 24K?
18K White Gold. Its machinability rates good (58/100) against poor (30/100) for 24K; for welding the order is 24K first (excellent, 90/100) then 18K White Gold (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 18K White Gold and 24K side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.