Precious Metal 14K vs 24K
Precious Metal · grade comparison
Precious Metal 14K and 24K are both precious metal grades. 14K is the stronger of the two: yield strength 220 MPa (31.9 ksi) against 30 MPa (4.35 ksi) for 24K, about 7.3 times as much; tensile strength follows at 400 MPa (58 ksi) vs 125 MPa (18.1 ksi). In exchange, 24K is the more ductile: elongation 45% versus 35% for 14K, and 14K is harder (133 HB vs 25 HB). 14K is lighter (13.07 g/cm³ vs 19.32 g/cm³ for 24K) and 24K runs hotter in service (600°C vs 250°C continuous). On the shop floor, 14K machines more easily (good vs poor) and 24K welds better (excellent vs very good).
14KChoose it when strength drives the design, or when weight is the constraint.
24KChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
14K vs 24K: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Castability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 14K | 24K |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
14K vs 24K — frequently asked
Is 14K stronger than 24K?
Yes. 14K has a typical yield strength of 220 MPa (31.9 ksi) against 30 MPa (4.35 ksi) for 24K — about 7.3 times as much. Tensile strength is 400 MPa (58 ksi) vs 125 MPa (18.1 ksi).
Which is cheaper, 14K or 24K?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 14K or 24K?
14K. Its machinability rates good (55/100) against poor (30/100) for 24K; for welding the order is 24K first (excellent, 90/100) then 14K (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 14K and 24K side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.