PESU-GF30 vs PSU-GF30
Polymer · grade comparison
PESU-GF30 and PSU-GF30 are both polymer grades. PESU-GF30 is the stronger of the two: tensile strength 150 MPa (21.8 ksi) against 108 MPa (15.7 ksi) for PSU-GF30, about 39% more. PSU-GF30 is lighter (1.49 g/cm³ vs 1.6 g/cm³ for PESU-GF30) and PESU-GF30 is stiffer (9.5 GPa vs 8.8 GPa). On the shop floor, PESU-GF30 welds better (50 vs 40 out of 100).
PESU-GF30Choose it when strength drives the design, or when the part sees heat.
PSU-GF30Choose it when weight is the constraint.
PESU-GF30 vs PSU-GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Hardness, Shore D
Hardness, Rockwell M
Fracture Toughness (K_IC)
Hardness, Rockwell R
Same in both: Elongation at Break 2.5% · Izod Impact, Notched 85 J/m1.6 ft·lbf/in
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Specific Heat Capacity 1,100 J/kg·K0.26 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22 µm/m·K12.2 µin/in·°F
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 150 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 85 / 100 · UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Same in both: Polishability 30 / 100 · Mold Shrinkage 0.3%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Same in both: Embodied Carbon (primary production) 7.5 kg CO₂/kg · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Same in both: Specific Stiffness (E / density) 5.9 MN·m/kg · Thermal Diffusivity 0.2 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | PESU-GF30 | PSU-GF30 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
PESU-GF30 vs PSU-GF30 — frequently asked
Is PESU-GF30 stronger than PSU-GF30?
Yes. PESU-GF30 has a typical tensile strength of 150 MPa (21.8 ksi) against 108 MPa (15.7 ksi) for PSU-GF30 — about 39% more.
Which is cheaper, PESU-GF30 or PSU-GF30?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, PESU-GF30 or PSU-GF30?
PSU-GF30, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for PESU-GF30; for welding the order is PESU-GF30 first (fair, 50/100) then PSU-GF30 (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PESU-GF30 and PSU-GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.