PBT GF15 vs PBT GF30
Polymer · grade comparison
PBT GF15 and PBT-GF30 are both polymer grades, compared here in the GF15 condition. PBT-GF30 is the stronger of the two: tensile strength 130 MPa (18.9 ksi) against 95 MPa (13.8 ksi) for PBT GF15, about 37% more. In exchange, PBT GF15 is the more ductile: elongation 3.5% versus 3% for PBT-GF30. PBT GF15 is lighter (1.42 g/cm³ vs 1.53 g/cm³ for PBT-GF30) and PBT-GF30 is stiffer (10 GPa vs 5.6 GPa). On the shop floor, PBT GF15 welds better (very good vs fair).
PBT GF15Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PBT-GF30Choose it when strength drives the design.
PBT GF15 vs PBT-GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Hardness, Rockwell R
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Same in both: Melting Temperature (Tm) 225°C437 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Max Service Temperature (continuous) 130°C266 °F · Min Service Temperature -40°C-40 °F · Heat Deflection Temp. @ 0.45 MPa 215°C419 °F
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Comparative Tracking Index (CTI)
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dissipation Factor (1 MHz) 0.02 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
UV / Weathering Resistance
Same in both: Corrosion Resistance 82 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Same in both: Machinability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | PBT GF15 | PBT-GF30 |
|---|---|---|
| Injection molding | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Chrome Plating (Plastic) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| UV Coating | Yes | — |
PBT GF15 vs PBT-GF30 — frequently asked
Is PBT-GF30 stronger than PBT GF15?
Yes. PBT-GF30 has a typical tensile strength of 130 MPa (18.9 ksi) against 95 MPa (13.8 ksi) for PBT GF15 — about 37% more.
Which is cheaper, PBT GF15 or PBT-GF30?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, PBT GF15 or PBT-GF30?
PBT GF15. Its weldability rates very good (70/100) against fair (45/100) for PBT-GF30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PBT GF15 and PBT-GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.