LDPE and PE-RT are both polymer grades. PE-RT is the stronger of the two: yield strength 18 MPa (2.61 ksi) against 10 MPa (1.45 ksi) for LDPE, about 80% more; tensile strength follows at 24 MPa (3.48 ksi) vs 11 MPa (1.6 ksi). PE-RT is the more ductile: elongation 750% versus 450% for LDPE, and PE-RT is harder (56 Shore D vs 47 Shore D). PE-RT is stiffer (0.8 GPa vs 0.22 GPa) and PE-RT conducts heat better (0.4 W/m·K vs 0.33 W/m·K). On the shop floor, PE-RT machines more easily (good vs fair) and LDPE sits in a lower cost tier (budget, $) than PE-RT (standard, $$).
LDPEChoose it when cost is the deciding factor.
PE-RTChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
LDPE vs PE-RT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore A
Hardness, Shore D
Tear Strength
Hardness, Rockwell R
Same in both: Poisson's Ratio 0.45
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Same in both: Glass Transition (Tg) -110°C-166 °F · Water Absorption (24 h) 0.01%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Max Service Temperature (short-term)
Same in both: Max Service Temperature (continuous) 70°C158 °F · Limiting Oxygen Index 18%
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dissipation Factor (1 MHz) 3×10⁻⁴ · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Same in both: Polishability 30 / 100 · Mold Temperature (typ.) 30°C86 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 80 MJ/kg34,394 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 0.2 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | LDPE | PE-RT |
|---|---|---|
| Sheet metal | Yes | — |
| Injection molding | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Chrome Plating (Plastic) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Painting | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| UV Coating | Yes | — |
LDPE vs PE-RT — frequently asked
Is PE-RT stronger than LDPE?
Yes. PE-RT has a typical yield strength of 18 MPa (2.61 ksi) against 10 MPa (1.45 ksi) for LDPE — about 80% more. Tensile strength is 24 MPa (3.48 ksi) vs 11 MPa (1.6 ksi).
Which is cheaper, LDPE or PE-RT?
LDPE is the lower-cost material: it sits in the budget tier ($) while PE-RT is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, LDPE or PE-RT?
PE-RT. Its machinability rates good (55/100) against fair (45/100) for LDPE.
Ready to make it?
Upload a CAD file and FabDigit prices the part in LDPE and PE-RT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.