CPE vs LDPE
Polymer · grade comparison
CPE and LDPE are both polymer grades. LDPE is the stronger of the two: tensile strength 11 MPa (1.6 ksi) against 8 MPa (1.16 ksi) for CPE, about 38% more. In exchange, CPE is the more ductile: elongation 700% versus 450% for LDPE, and LDPE is harder (47 Shore D vs 18 Shore D). LDPE is lighter (0.92 g/cm³ vs 1.16 g/cm³ for CPE) and LDPE is stiffer (0.22 GPa vs 0.02 GPa). On the shop floor, LDPE machines more easily (fair vs poor) and LDPE welds better (excellent vs very good).
CPEChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
LDPEChoose it when strength drives the design, or when weight is the constraint.
CPE vs LDPE: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Hardness, Shore A
Hardness, Shore D
Tear Strength
Compression Set (22 h, 70 °C)
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Melting Temperature (Tm)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Limiting Oxygen Index
Max Service Temperature (short-term)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Polishability
Mold Shrinkage
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Melt Flow Rate
Same in both: Formability (cold) 90 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | CPE | LDPE |
|---|---|---|
| Sheet metal | — | Yes |
| Injection molding | — | Yes |
| Default condition | — | Unfilled |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Chrome Plating (Plastic) | — | Yes |
| EMI Shielding Coating | — | Yes |
| Painting | — | Yes |
| Soft Touch Coating | — | Yes |
| Spray Painting | — | Yes |
| UV Coating | — | Yes |
CPE vs LDPE — frequently asked
Is LDPE stronger than CPE?
Yes. LDPE has a typical tensile strength of 11 MPa (1.6 ksi) against 8 MPa (1.16 ksi) for CPE — about 38% more.
Which is cheaper, CPE or LDPE?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, CPE or LDPE?
LDPE. Its machinability rates fair (45/100) against poor (25/100) for CPE; for welding the order is LDPE first (excellent, 95/100) then CPE (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in CPE and LDPE side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.