Nickel Alloy Hastelloy C-2000 vs Hastelloy C276
Nickel Alloy · grade comparison
Nickel Alloy Hastelloy C-2000 and Hastelloy C276 are both nickel alloy grades. Both yield at about 355 MPa — strength does not separate them. Hastelloy C276 is harder — 194 HB against 175 HB for Hastelloy C-2000 — which matters for wear surfaces and threads. Hastelloy C-2000 is lighter (8.5 g/cm³ vs 8.89 g/cm³ for Hastelloy C276) and Hastelloy C276 conducts heat better (10.2 W/m·K vs 9.1 W/m·K). On the shop floor, Hastelloy C276 sits in a lower cost tier (premium, $$$) than Hastelloy C-2000 (high, $$$$).
Hastelloy C-2000Choose it when weight is the constraint.
Hastelloy C276Choose it when surface hardness matters, or when cost is the deciding factor.
Hastelloy C-2000 vs Hastelloy C276: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Hastelloy C-2000Hastelloy C276
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Shear Modulus 79 GPa11.5 Msi · Poisson's Ratio 0.31 · Reduction in Area 65%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Machinability 18 / 100 · Machinability Rating (AISI 1212 = 100 %) 12% · Weldability 85 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Strength (UTS / density) 89 kN·m/kg
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Hastelloy C-2000 | Hastelloy C276 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Solution Annealed |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | 1.5 mm |
| Best machined surface | — | Ra 1.6 µm |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
They share 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Hastelloy C-2000 vs Hastelloy C276 — frequently asked
What is the difference between Hastelloy C-2000 and Hastelloy C276?
Nickel Alloy Hastelloy C-2000 and Hastelloy C276 are both nickel alloy grades. Both yield at about 355 MPa — strength does not separate them. Hastelloy C276 is harder — 194 HB against 175 HB for Hastelloy C-2000 — which matters for wear surfaces and threads.
Which is cheaper, Hastelloy C-2000 or Hastelloy C276?
Hastelloy C276 is the lower-cost material: it sits in the premium tier ($$$) while Hastelloy C-2000 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Hastelloy C-2000 over Hastelloy C276?
Pick Hastelloy C-2000 when weight is the constraint. Pick Hastelloy C276 when surface hardness matters, or when cost is the deciding factor.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hastelloy C-2000 and Hastelloy C276 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.