Nickel Alloy Alloy 22 vs Hastelloy G-3
Nickel Alloy · grade comparison
Nickel Alloy Alloy 22 and Hastelloy G-3 are both nickel alloy grades. Alloy 22 is the stronger of the two: yield strength 400 MPa (58 ksi) against 310 MPa (45 ksi) for Hastelloy G-3, about 29% more; tensile strength follows at 800 MPa (116 ksi) vs 690 MPa (100 ksi). Alloy 22 is the more ductile: elongation 62% versus 50% for Hastelloy G-3, and Alloy 22 is harder (200 HB vs 185 HB). Hastelloy G-3 is lighter (8.31 g/cm³ vs 8.69 g/cm³ for Alloy 22). On the shop floor, Hastelloy G-3 machines more easily (25 vs 15 out of 100).
Alloy 22Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Hastelloy G-3Choose it when weight is the constraint, or when the part is machined in volume.
Alloy 22 vs Hastelloy G-3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Charpy V-Notch Impact (RT) 250 J184 ft·lbf · Hardness, Rockwell B 88 HRB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.5 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Polishability
Same in both: Weldability 85 / 100 · Brazeability / Solderability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 12 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Alloy 22 | Hastelloy G-3 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Alloy 22 vs Hastelloy G-3 — frequently asked
Is Alloy 22 stronger than Hastelloy G-3?
Yes. Alloy 22 has a typical yield strength of 400 MPa (58 ksi) against 310 MPa (45 ksi) for Hastelloy G-3 — about 29% more. Tensile strength is 800 MPa (116 ksi) vs 690 MPa (100 ksi).
Which is cheaper, Alloy 22 or Hastelloy G-3?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Alloy 22 or Hastelloy G-3?
Hastelloy G-3, by a small margin. Both rate poor for machinability — 25/100 against 15/100 for Alloy 22.