Magnesium Alloy AS41B vs ZC63A
Magnesium Alloy · grade comparison
Magnesium Alloy AS41B and ZC63A are both magnesium alloy grades. Both yield at about 140 MPa — strength does not separate them. AS41B is the more ductile: elongation 6% versus 5% for ZC63A, and AS41B is harder (75 HB vs 60 HB). AS41B is lighter (1.77 g/cm³ vs 1.87 g/cm³ for ZC63A) and AS41B runs hotter in service (175°C vs 150°C continuous). On the shop floor, AS41B sits in a lower cost tier (standard, $$) than ZC63A (premium, $$$).
AS41BChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
AS41B vs ZC63A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Reduction in Area
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 45 GPa6.5 Msi · Shear Modulus 17 GPa2.5 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35 · Shear Strength 140 MPa20.3 ksi · Fracture Toughness (K_IC) 13 MPa·√m11.8 ksi·√in · Charpy V-Notch Impact (RT) 3 J2.2 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 340 J/g146 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 95 / 100 · Formability (cold) 10 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 500 L/kg59.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AS41B | ZC63A |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
AS41B vs ZC63A — frequently asked
What is the difference between AS41B and ZC63A?
Magnesium Alloy AS41B and ZC63A are both magnesium alloy grades. Both yield at about 140 MPa — strength does not separate them. AS41B is the more ductile: elongation 6% versus 5% for ZC63A, and AS41B is harder (75 HB vs 60 HB).
Which is cheaper, AS41B or ZC63A?
AS41B is the lower-cost material: it sits in the standard tier ($$) while ZC63A is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, AS41B or ZC63A?
ZC63A. Its weldability rates fair (40/100) against fair (35/100) for AS41B.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AS41B and ZC63A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.