C-Glass vs Gorilla Glass
Glass · grade comparison
C-Glass and Gorilla Glass are both glass grades. C-Glass is the stronger of the two: tensile strength 3,300 MPa (479 ksi) against 350 MPa (50.8 ksi) for Gorilla Glass, about 9.4 times as much. C-Glass is the more ductile: elongation 4.8% versus 0% for Gorilla Glass, and Gorilla Glass is harder (620 HV vs 540 HV). Gorilla Glass is lighter (2.42 g/cm³ vs 2.52 g/cm³ for C-Glass) and C-Glass runs hotter in service (480°C vs 200°C continuous).
C-GlassChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Gorilla GlassChoose it when weight is the constraint.
C-Glass vs Gorilla Glass: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all glass grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all glass grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Same in both: Compressive Strength 1,000 MPa145 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Refractive Index
Light Transmission
Same in both: Porosity 0%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 0.5 mm²/s
Strength versus weight
Yield strength against density for every glass grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C-Glass | Gorilla Glass |
|---|---|---|
| Default condition | — | Chem Strengthened |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
C-Glass vs Gorilla Glass — frequently asked
Is C-Glass stronger than Gorilla Glass?
Yes. C-Glass has a typical tensile strength of 3,300 MPa (479 ksi) against 350 MPa (50.8 ksi) for Gorilla Glass — about 9.4 times as much.
Which is cheaper, C-Glass or Gorilla Glass?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C-Glass or Gorilla Glass?
C-Glass, by a small margin. Both rate not recommended for machinability — 12/100 against 5/100 for Gorilla Glass.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C-Glass and Gorilla Glass side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.