C-Glass vs Soda-Lime Glass
Glass · grade comparison
C-Glass and Soda-Lime Glass are both glass grades. C-Glass is the stronger of the two: tensile strength 3,300 MPa (479 ksi) against 45 MPa (6.53 ksi) for Soda-Lime Glass, about 73 times as much. C-Glass is the more ductile: elongation 4.8% versus 0% for Soda-Lime Glass. C-Glass runs hotter in service (480°C vs 110°C continuous). On the shop floor, Soda-Lime Glass sits in a lower cost tier (budget, $) than C-Glass (standard, $$).
C-GlassChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Soda-Lime GlassChoose it when cost is the deciding factor.
C-Glass vs Soda-Lime Glass: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all glass grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all glass grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Same in both: Bulk Modulus 43 GPa6.2 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Refractive Index
Light Transmission
Same in both: Porosity 0%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Same in both: Electrical Resistivity 1×10¹⁰ Ω·m3.94×10¹⁷ µΩ·in · Dielectric Strength 12 kV/mm305 V/mil · Volume Resistivity 1×10¹² Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 0.5 mm²/s
Strength versus weight
Yield strength against density for every glass grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C-Glass | Soda-Lime Glass |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
C-Glass vs Soda-Lime Glass — frequently asked
Is C-Glass stronger than Soda-Lime Glass?
Yes. C-Glass has a typical tensile strength of 3,300 MPa (479 ksi) against 45 MPa (6.53 ksi) for Soda-Lime Glass — about 73 times as much.
Which is cheaper, C-Glass or Soda-Lime Glass?
Soda-Lime Glass is the lower-cost material: it sits in the budget tier ($) while C-Glass is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C-Glass or Soda-Lime Glass?
Soda-Lime Glass. Its machinability rates poor (20/100) against not recommended (12/100) for C-Glass.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C-Glass and Soda-Lime Glass side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.