Copper Alloy C95200 vs C95500
Copper Alloy · grade comparison
Copper Alloy C95200 and C95500 are both copper alloy grades. C95500 is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 207 MPa (30 ksi) for C95200, about 45% more; tensile strength follows at 700 MPa (102 ksi) vs 552 MPa (80.1 ksi). In exchange, C95200 is the more ductile: elongation 30% versus 8% for C95500, and C95500 is harder (192 HB vs 115 HB). C95200 conducts heat better (58.6 W/m·K vs 42 W/m·K). On the shop floor, C95200 welds better (very good vs good) and C95200 sits in a lower cost tier (high, $$$$) than C95500 (specialty, $$$$$).
C95200Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C95500Choose it when strength drives the design.
C95200 vs C95500: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Poisson's Ratio 0.32
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Max Service Temperature (continuous) 300°C572 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 50% · Castability 75 / 100 · Brazeability / Solderability 30 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 250 L/kg30 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C95200 | C95500 |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | — | As Cast |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| Chrome Plating | — | Yes |
| Electropolishing | — | Yes |
| Nickel Plating | — | Yes |
| Painting | — | Yes |
| Tin Plating | — | Yes |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C95200 vs C95500 — frequently asked
Is C95500 stronger than C95200?
Yes. C95500 has a typical yield strength of 300 MPa (43.5 ksi) against 207 MPa (30 ksi) for C95200 — about 45% more. Tensile strength is 700 MPa (102 ksi) vs 552 MPa (80.1 ksi).
Which is cheaper, C95200 or C95500?
C95200 is the lower-cost material: it sits in the high tier ($$$$) while C95500 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C95200 or C95500?
C95200, by a small margin. Both rate fair for machinability — 45/100 against 40/100 for C95500; for welding the order is C95200 first (very good, 70/100) then C95500 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C95200 and C95500 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.