Copper Alloy C75400-H01 vs C75400-H02
Copper Alloy · C75400 temper comparison
C75400-H01 and C75400-H02 are two conditions of the same copper alloy grade, C75400: H01 (quarter hard) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. C75400-H02 is the stronger of the two: yield strength 425 MPa (61.6 ksi) against 320 MPa (46.4 ksi) for C75400-H01, about 33% more; tensile strength follows at 515 MPa (74.7 ksi) vs 460 MPa (66.7 ksi). In exchange, C75400-H01 is the more ductile: elongation 20% versus 12% for C75400-H02, and C75400-H02 is harder (140 HB vs 118 HB). C75400-H01 runs hotter in service (220°C vs 200°C continuous).
C75400-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C75400-H02Choose it when strength drives the design.
C75400-H01 vs C75400-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 125 GPa18.1 Msi · Shear Modulus 47 GPa6.8 Msi · Bulk Modulus 122 GPa17.7 Msi · Poisson's Ratio 0.33 · Hardness, Vickers 150 HV
Physical
Density and transition temperatures.
Same in both: Density 8.72 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,021°C1,870 °F · Liquidus Temperature 1,054°C1,929 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 37 W/m·K21.4 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6.5 % IACS · Electrical Resistivity 2.65×10⁻⁷ Ω·m10.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V · Corrosion Resistance 66 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 45 / 100 · Brazeability / Solderability 80 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C75400-H01 vs C75400-H02 — frequently asked
Is C75400-H02 stronger than C75400-H01?
Yes. C75400-H02 has a typical yield strength of 425 MPa (61.6 ksi) against 320 MPa (46.4 ksi) for C75400-H01 — about 33% more. Tensile strength is 515 MPa (74.7 ksi) vs 460 MPa (66.7 ksi).
Which condition does FabDigit quote by default, H01 or H02?
H02 is the default C75400 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C75400-H01 over C75400-H02?
Pick C75400-H01 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C75400-H02 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C75400-H01 and C75400-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.