Copper Alloy C75400-H02 vs C75400-H04
Copper Alloy · C75400 temper comparison
C75400-H02 and C75400-H04 are two conditions of the same copper alloy grade, C75400: H02 (half hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. C75400-H04 is the stronger of the two: yield strength 510 MPa (74 ksi) against 425 MPa (61.6 ksi) for C75400-H02, about 20% more; tensile strength follows at 585 MPa (84.8 ksi) vs 515 MPa (74.7 ksi). In exchange, C75400-H02 is the more ductile: elongation 12% versus 5% for C75400-H04, and C75400-H04 is harder (165 HB vs 140 HB). C75400-H02 runs hotter in service (200°C vs 180°C continuous).
C75400-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C75400-H04Choose it when strength drives the design.
C75400-H02 vs C75400-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 125 GPa18.1 Msi · Shear Modulus 47 GPa6.8 Msi · Bulk Modulus 122 GPa17.7 Msi · Poisson's Ratio 0.33 · Hardness, Vickers 150 HV
Physical
Density and transition temperatures.
Same in both: Density 8.72 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,021°C1,870 °F · Liquidus Temperature 1,054°C1,929 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 37 W/m·K21.4 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6.5 % IACS · Electrical Resistivity 2.65×10⁻⁷ Ω·m10.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V · Corrosion Resistance 66 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Brazeability / Solderability 80 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C75400-H02 vs C75400-H04 — frequently asked
Is C75400-H04 stronger than C75400-H02?
Yes. C75400-H04 has a typical yield strength of 510 MPa (74 ksi) against 425 MPa (61.6 ksi) for C75400-H02 — about 20% more. Tensile strength is 585 MPa (84.8 ksi) vs 515 MPa (74.7 ksi).
Which condition does FabDigit quote by default, H02 or H04?
H02 is the default C75400 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C75400-H02 over C75400-H04?
Pick C75400-H02 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C75400-H04 when strength drives the design.