Boron Fiber Composite vs Kevlar 149
Composite · grade comparison
Boron Fiber Composite and Kevlar 149 are both composite grades. Kevlar 149 is the stronger of the two: tensile strength 3,400 MPa (493 ksi) against 1,500 MPa (218 ksi) for Boron Fiber Composite, about 127% more. Kevlar 149 is the more ductile: elongation 1.5% versus 0.75% for Boron Fiber Composite. Kevlar 149 is lighter (1.47 g/cm³ vs 2 g/cm³ for Boron Fiber Composite) and Boron Fiber Composite is stiffer (205 GPa vs 175 GPa). On the shop floor, Kevlar 149 machines more easily (poor vs not recommended).
Kevlar 149Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Boron Fiber Composite vs Kevlar 149: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Boron Fiber CompositeKevlar 149
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Boron Fiber Composite | Kevlar 149 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Boron Fiber Composite vs Kevlar 149 — frequently asked
Is Kevlar 149 stronger than Boron Fiber Composite?
Yes. Kevlar 149 has a typical tensile strength of 3,400 MPa (493 ksi) against 1,500 MPa (218 ksi) for Boron Fiber Composite — about 127% more.
Which is cheaper, Boron Fiber Composite or Kevlar 149?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Boron Fiber Composite or Kevlar 149?
Kevlar 149. Its machinability rates poor (25/100) against not recommended (8/100) for Boron Fiber Composite.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Boron Fiber Composite and Kevlar 149 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.