Cr3C2 vs TiC
Ceramic · grade comparison
Cr3C2 and TiC are both ceramic grades. TiC is harder — 3,000 HV against 1,400 HV for Cr3C2 — which matters for wear surfaces and threads. TiC is lighter (4.93 g/cm³ vs 6.68 g/cm³ for Cr3C2) and TiC is stiffer (445 GPa vs 373 GPa).
Cr3C2Choose it when the part sees heat.
TiCChoose it when surface hardness matters, or when weight is the constraint.
Cr3C2 vs TiC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Typical Recycled Content 5%
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Thermal Diffusivity
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Cr3C2 | TiC |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Cr3C2 vs TiC — frequently asked
What is the difference between Cr3C2 and TiC?
Cr3C2 and TiC are both ceramic grades. TiC is harder — 3,000 HV against 1,400 HV for Cr3C2 — which matters for wear surfaces and threads. TiC is lighter (4.93 g/cm³ vs 6.68 g/cm³ for Cr3C2) and TiC is stiffer (445 GPa vs 373 GPa).
Which is cheaper, Cr3C2 or TiC?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose Cr3C2 over TiC?
Pick Cr3C2 when the part sees heat. Pick TiC when surface hardness matters, or when weight is the constraint.