B4C vs Cr3C2
Ceramic · grade comparison
B4C and Cr3C2 are both ceramic grades. B4C is the stronger of the two: tensile strength 300 MPa (43.5 ksi) against 200 MPa (29 ksi) for Cr3C2, about 50% more. B4C is harder — 3,000 HV against 1,400 HV for Cr3C2 — which matters for wear surfaces and threads. B4C is lighter (2.51 g/cm³ vs 6.68 g/cm³ for Cr3C2) and B4C is stiffer (450 GPa vs 373 GPa).
B4CChoose it when strength drives the design, or when surface hardness matters.
Cr3C2Choose it when the part sees heat.
B4C vs Cr3C2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Elongation at Break
Same in both: Flexural Strength 400 MPa58 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | B4C | Cr3C2 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
B4C vs Cr3C2 — frequently asked
Is B4C stronger than Cr3C2?
Yes. B4C has a typical tensile strength of 300 MPa (43.5 ksi) against 200 MPa (29 ksi) for Cr3C2 — about 50% more.
Which is cheaper, B4C or Cr3C2?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose B4C over Cr3C2?
Pick B4C when strength drives the design, or when surface hardness matters. Pick Cr3C2 when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in B4C and Cr3C2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.