BeO Ceramic vs TiO2 Ceramic
Ceramic · grade comparison
BeO Ceramic and TiO2 Ceramic are both ceramic grades. BeO Ceramic is the stronger of the two: tensile strength 140 MPa (20.3 ksi) against 80 MPa (11.6 ksi) for TiO2 Ceramic, about 75% more. BeO Ceramic is harder — 1,200 HV against 950 HV for TiO2 Ceramic — which matters for wear surfaces and threads. BeO Ceramic is lighter (2.87 g/cm³ vs 4.15 g/cm³ for TiO2 Ceramic) and BeO Ceramic is stiffer (345 GPa vs 250 GPa).
BeO CeramicChoose it when strength drives the design, or when surface hardness matters.
BeO Ceramic vs TiO2 Ceramic: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Flexural Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Refractive Index
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Sintering / Firing Temperature
Same in both: Machinability 5 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BeO Ceramic | TiO2 Ceramic |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BeO Ceramic vs TiO2 Ceramic — frequently asked
Is BeO Ceramic stronger than TiO2 Ceramic?
Yes. BeO Ceramic has a typical tensile strength of 140 MPa (20.3 ksi) against 80 MPa (11.6 ksi) for TiO2 Ceramic — about 75% more.
Which is cheaper, BeO Ceramic or TiO2 Ceramic?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose BeO Ceramic over TiO2 Ceramic?
Pick BeO Ceramic when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in BeO Ceramic and TiO2 Ceramic side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.