Al2TiO5 vs BeO Ceramic
Ceramic · grade comparison
Al2TiO5 and BeO Ceramic are both ceramic grades. BeO Ceramic is the stronger of the two: tensile strength 140 MPa (20.3 ksi) against 15 MPa (2.18 ksi) for Al2TiO5, about 9.3 times as much. BeO Ceramic is harder — 1,200 HV against 450 HV for Al2TiO5 — which matters for wear surfaces and threads. BeO Ceramic is lighter (2.87 g/cm³ vs 3.2 g/cm³ for Al2TiO5) and BeO Ceramic is stiffer (345 GPa vs 15 GPa). On the shop floor, Al2TiO5 machines more easily (poor vs not recommended).
Al2TiO5Choose it when the part is machined in volume.
BeO CeramicChoose it when strength drives the design, or when surface hardness matters.
Al2TiO5 vs BeO Ceramic: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Mohs
Hardness, Knoop
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Refractive Index
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Al2TiO5 | BeO Ceramic |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Al2TiO5 vs BeO Ceramic — frequently asked
Is BeO Ceramic stronger than Al2TiO5?
Yes. BeO Ceramic has a typical tensile strength of 140 MPa (20.3 ksi) against 15 MPa (2.18 ksi) for Al2TiO5 — about 9.3 times as much.
Which is cheaper, Al2TiO5 or BeO Ceramic?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Al2TiO5 or BeO Ceramic?
Al2TiO5. Its machinability rates poor (25/100) against not recommended (5/100) for BeO Ceramic.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Al2TiO5 and BeO Ceramic side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.