Aluminum 4043 vs 4045
Aluminum · grade comparison
Aluminum 4043 and 4045 are both aluminum grades, both heat resistant al. 4043 is the stronger of the two: yield strength 120 MPa (17.4 ksi) against 45 MPa (6.53 ksi) for 4045, about 167% more; tensile strength follows at 180 MPa (26.1 ksi) vs 110 MPa (16 ksi). In exchange, 4045 is the more ductile: elongation 20% versus 12% for 4043, and 4043 is harder (50 HB vs 30 HB). 4043 runs hotter in service (200°C vs 150°C continuous). On the shop floor, 4043 welds better (excellent vs very good).
4043Choose it when strength drives the design, or when the part sees heat.
4045Choose it when the part is bent, formed or impact-loaded.
4043 vs 4045: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Castability
Brazeability / Solderability
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Formability (cold) 70 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4043 | 4045 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | — | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| DLC | Yes | — |
Both are offered for Sheet metal. They share 15 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating, PTFE Coating and 3 more.
4043 vs 4045 — frequently asked
Is 4043 stronger than 4045?
Yes. 4043 has a typical yield strength of 120 MPa (17.4 ksi) against 45 MPa (6.53 ksi) for 4045 — about 167% more. Tensile strength is 180 MPa (26.1 ksi) vs 110 MPa (16 ksi).
Which is cheaper, 4043 or 4045?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 4043 or 4045?
4045. Its machinability rates fair (38/100) against poor (30/100) for 4043; for welding the order is 4043 first (excellent, 95/100) then 4045 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4043 and 4045 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.