Aluminum 393.0-T6 vs 393.0-T7
Aluminum · 393.0 temper comparison
393.0-T6 and 393.0-T7 are two conditions of the same aluminum grade, 393.0: T6 (solution heat treated and artificially aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. 393.0-T6 is the stronger of the two: yield strength 275 MPa (39.9 ksi) against 230 MPa (33.4 ksi) for 393.0-T7, about 20% more; tensile strength follows at 290 MPa (42.1 ksi) vs 250 MPa (36.3 ksi). In exchange, 393.0-T7 is the more ductile: elongation 1% versus 0.7% for 393.0-T6, and 393.0-T6 is harder (140 HB vs 120 HB). 393.0-T7 runs hotter in service (300°C vs 250°C continuous).
393.0-T6Choose it when strength drives the design.
393.0-T7Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
393.0-T6 vs 393.0-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 88 GPa12.8 Msi · Shear Modulus 33 GPa4.8 Msi · Bulk Modulus 72 GPa10.4 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 555°C1,031 °F · Liquidus Temperature 705°C1,301 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 960 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15.8 µm/m·K8.8 µin/in·°F · Latent Heat of Fusion 500 J/g215 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.81 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 70 / 100 · Brazeability / Solderability 20 / 100 · Polishability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 190 MJ/kg81,685 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
393.0-T6 vs 393.0-T7 — frequently asked
Is 393.0-T6 stronger than 393.0-T7?
Yes. 393.0-T6 has a typical yield strength of 275 MPa (39.9 ksi) against 230 MPa (33.4 ksi) for 393.0-T7 — about 20% more. Tensile strength is 290 MPa (42.1 ksi) vs 250 MPa (36.3 ksi).
Which condition does FabDigit quote by default, T6 or T7?
T6 is the default 393.0 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 393.0-T6 over 393.0-T7?
Pick 393.0-T6 when strength drives the design. Pick 393.0-T7 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 393.0-T6 and 393.0-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.