Aluminum 356 vs 444.0
Aluminum · grade comparison
Aluminum 356 and 444.0 are both aluminum grades. 356 is the stronger of the two: yield strength 186 MPa (27 ksi) against 62 MPa (8.99 ksi) for 444.0, about 3.0 times as much; tensile strength follows at 262 MPa (38 ksi) vs 145 MPa (21 ksi). In exchange, 444.0 is the more ductile: elongation 12% versus 5% for 356, and 356 is harder (80 HB vs 44 HB). On the shop floor, 356 machines more easily (very good vs fair) and 356 sits in a lower cost tier (budget, $) than 444.0 (standard, $$).
356Choose it when strength drives the design, or when the part is machined in volume.
444.0Choose it when the part is bent, formed or impact-loaded.
356 vs 444.0: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 557°C1,035 °F · Liquidus Temperature 613°C1,135 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 151 W/m·K87.2 BTU/hr·ft·°F · Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.5 µm/m·K11.9 µin/in·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 356 | 444.0 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
356 vs 444.0 — frequently asked
Is 356 stronger than 444.0?
Yes. 356 has a typical yield strength of 186 MPa (27 ksi) against 62 MPa (8.99 ksi) for 444.0 — about 3.0 times as much. Tensile strength is 262 MPa (38 ksi) vs 145 MPa (21 ksi).
Which is cheaper, 356 or 444.0?
356 is the lower-cost material: it sits in the budget tier ($) while 444.0 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 356 or 444.0?
356. Its machinability rates very good (70/100) against fair (50/100) for 444.0.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 356 and 444.0 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.