Aluminum 2008-O vs 2008-T62
Aluminum · 2008 temper comparison
2008-O and 2008-T62 are two conditions of the same aluminum grade, 2008: O (annealed) versus T62 (T6, heat treated by the user). The chemistry is identical, so every difference below comes from the condition. 2008-T62 is the stronger of the two: yield strength 270 MPa (39.2 ksi) against 60 MPa (8.7 ksi) for 2008-O, about 4.5 times as much; tensile strength follows at 310 MPa (45 ksi) vs 130 MPa (18.9 ksi). In exchange, 2008-O is the more ductile: elongation 32% versus 12% for 2008-T62, and 2008-T62 is harder (93 HB vs 38 HB). 2008-T62 runs hotter in service (150°C vs 120°C continuous). On the shop floor, 2008-T62 machines more easily (65 vs 55 out of 100).
2008-OChoose it when the part is bent, formed or impact-loaded.
2008-T62Choose it when strength drives the design, or when the part sees heat.
2008-O vs 2008-T62: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.72 g/cm³0.1 lb/in³ · Melting Point (Solidus) 560°C1,040 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 200 W/m·K116 BTU/hr·ft·°F · Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 15 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2008-O vs 2008-T62 — frequently asked
Is 2008-T62 stronger than 2008-O?
Yes. 2008-T62 has a typical yield strength of 270 MPa (39.2 ksi) against 60 MPa (8.7 ksi) for 2008-O — about 4.5 times as much. Tensile strength is 310 MPa (45 ksi) vs 130 MPa (18.9 ksi).
Which condition does FabDigit quote by default, O or T62?
T4 is the default 2008 condition in the FabDigit quote flow (neither O nor T62). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2008-O or 2008-T62?
2008-T62, by a small margin. Both rate good for machinability — 65/100 against 55/100 for 2008-O; for welding the order is 2008-O first (fair, 35/100) then 2008-T62 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2008-O and 2008-T62 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.