PZT-5H
Grade
also Lead Zirconate Titanate
PZT-5H = very soft, high-permittivity Navy Type VI actuator/medical grade
Pick for maximum strain and charge output (multilayer actuators, medical imaging arrays) where the low Curie point and higher loss are acceptable.
Values for the PZT-5H condition
Other PZT tempers and conditions
PZT is listed in 5 conditions; see the grade overview at PZT.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
PZT-5HThis page Very soft, high-permittivity Navy Type VI actuator/medical grade | Pick for maximum strain and charge output (multilayer actuators, medical imaging arrays) where the low Curie point and higher loss are acceptable. | — | 70 | — | 300 HV | 2 W/m·K |
SinteredDefault conventionally pressed and sintered, poled (generic Navy Type II / PZT-5A class) | Default general-purpose soft PZT blank for sensors, receivers and low-power actuators. | — | 75 | — | 350 HV | 1 W/m·K |
Soft (donor-doped) Navy Type II, general sensing/receiving grade | Pick for hydrophones, accelerometers and low-drive actuators needing high sensitivity with good temperature stability. | — | 75 | — | 340 HV | 1 W/m·K |
Hard (acceptor-doped) Navy Type I, high-power transmitter grade | Pick for high-drive sonar and ultrasonic power transducers where low loss and high mechanical Q matter more than sensitivity. | — | 78 | — | 360 HV | 1 W/m·K |
Extra-hard Navy Type III, very high power / low loss grade | Pick for continuous high-field ultrasonic welding/cleaning stacks where dielectric and mechanical losses must be minimal. | — | 80 | — | 400 HV | 1 W/m·K |
What is PZT-5H?
PZT-5H is PZT in the PZT-5H grade — pick for maximum strain and charge output (multilayer actuators, medical imaging arrays) where the low Curie point and higher loss are acceptable. PZT-5H has a tensile strength of 70 MPa (10.2 ksi), weaker than 60% of ceramic grades. The elastic modulus is 60 GPa (8.7 Msi). PZT-5H has a density of 7.5 g/cm³ (0.271 lb/in³), heavier than 73% of ceramic grades. Sintered is the default condition FabDigit quotes; PZT-5H is available on request or by drawing note.
Limitations
- Low fracture toughness — 0.8 MPa·√m (0.728 ksi·√in), worse than 99% of ceramic grades
- Limited service temperature — 95°C (203 °F), worse than 97% of ceramic grades
- Poor heat conductor — 1.5 W/m·K (0.867 BTU/hr·ft·°F), worse than 92% of ceramic grades
- Low stiffness — 60 GPa (8.7 Msi), worse than 83% of ceramic grades
PZT-5H properties
Typical room-temperature values for PZT-5H; 15 are specific to this condition. Other listed values are PZT reference data and may not represent this condition. Bars are the position among ceramic grades.
Physical2
PZT-5H has a density of 7.5 g/cm³ (0.271 lb/in³), heavier than 73% of ceramic grades.
Mechanical11
PZT-5H has a tensile strength of 70 MPa (10.2 ksi), weaker than 60% of ceramic grades. The elastic modulus is 60 GPa (8.7 Msi).
Thermal5
PZT-5H is rated for continuous service to 95°C (203 °F). It conducts heat at 1.5 W/m·K (0.867 BTU/hr·ft·°F), worse than 92% of ceramic grades. Thermal expansion is 4 µm/m·K (2.22 µin/in·°F).
Electrical5
PZT-5H is an electrical insulator with a dielectric strength of 5 kV/mm (127 V/mil) and a resistivity of 1×10⁹ Ω·m.
Chemical & Environmental2
Corrosion resistance is good (58/100), worse than 72% of ceramic grades.
Sustainability4
Producing a kilogram of PZT-5H takes about 70 MJ of energy and emits 5.5 kg of CO₂ — less than 71% of ceramic grades. Typical recycled content is 5%.
Manufacturability3
PZT-5H's machinability is not recommended (9/100, better than 75% of ceramic grades).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PZT-5H
Is PZT easy to machine?
Green machining is easy; fired PZT requires diamond grinding, lapping, dicing or ultrasonic machining, with light passes to avoid edge chipping and micro-cracking.
Can PZT be welded?
Not weldable — joined by conductive epoxy, solder to fired-on Ag electrodes (<250 °C, short dwell) or clamped stack preload.
Can PZT be formed, bent or molded?
Formed by dry/isostatic pressing or tape casting of calcined powder, sintered 1150–1320 °C in a PbO-rich atmosphere to limit lead volatilisation, then electroded and DC-poled above the coercive field.
What surface finishes work on PZT?
Fired silver, sputtered Cr/Ni-Au or electroless Ni electrodes; lap or polish faces flat before electroding, and avoid temperatures above ~½ Tc during any downstream process to prevent depoling.
PZT chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Pbas PbO in the perovskite A-site; partly substituted by Sr/Ba/La in doped grades | 60 – 65 | 63.6 |
| ZrZr/Ti ratio near the morphotropic phase boundary (~52/48) | 12 – 16 | 14.6 |
| Ti | 6 – 8.5 | 7.1 |
| Nbdonor dopant in soft grades (PZT-5A/5H) | 0 – 1.5 | 0.6 |
| Feacceptor dopant in hard grades (PZT-4/8) | 0 – 1 | 0.3 |
| SrA-site modifier, adjusts Curie point/permittivity | 0 – 2 | 0.8 |
| O | ≥ 14 (balance) | — |
PZT-5H — frequently asked
What is PZT-5H used for?
PZT-5H is typically used for ultrasonic transducer discs and rings, piezoelectric sensors and accelerometers, hydrophone and sonar elements, stack and bender actuators, ultrasonic cleaning and welding drivers and flow and level measurement probes. In short: piezoelectric actuator ceramic.
What is the tensile strength of PZT-5H?
PZT-5H has a typical tensile strength of 70 MPa (10.2 ksi) — weaker than 60% of ceramic grades. Strength varies by condition: see the 5 listed tempers.
Is PZT-5H easy to machine?
Not especially — machinability is rated not recommended (9/100, better than 75% of ceramic grades). Green machining is easy; fired PZT requires diamond grinding, lapping, dicing or ultrasonic machining, with light passes to avoid edge chipping and micro-cracking.
Can PZT-5H be welded?
Not weldable — joined by conductive epoxy, solder to fired-on Ag electrodes (<250 °C, short dwell) or clamped stack preload.
What surface finishes work on PZT-5H?
Fired silver, sputtered Cr/Ni-Au or electroless Ni electrodes; lap or polish faces flat before electroding, and avoid temperatures above ~½ Tc during any downstream process to prevent depoling.
Can PZT-5H be formed, bent or molded?
Formed by dry/isostatic pressing or tape casting of calcined powder, sintered 1150–1320 °C in a PbO-rich atmosphere to limit lead volatilisation, then electroded and DC-poled above the coercive field.
What is the maximum service temperature of PZT-5H?
PZT-5H is rated for continuous use to about 95°C (203 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- IEEE 176 Standard on Piezoelectricity — IEEE (1987)
- Physical and Piezoelectric Properties of APC Materials — APC International (2023)
- PIC Piezoelectric Ceramic Materials Data — PI Ceramic (2023)
- ASM Engineered Materials Handbook Vol.4 — Ceramics and Glasses — ASM International (1991)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.