Zinc Alloy Slush Metal Stabilized
Heat-treated state
also Hollow Casting Zinc, Slush Zinc
Pick when the casting must hold close dimensions after machining or plating; trades a little strength for stability and ductility.
Values for the Stabilized condition
Other Slush Metal tempers and conditions
Slush Metal is listed in 5 conditions; see the grade overview at Slush Metal.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As Cast, Zamak 3 (Zn-4Al) base metal used for slush work | Cheapest and most stable option; narrow freezing range means thicker, less uniform slush shells but excellent platability. | 120 | 170 | 4 | 65 HB | 27 % IACS |
StabilizedThis page low-temperature dimensional stabilizing anneal (~100 °C, 3–6 h) | Pick when the casting must hold close dimensions after machining or plating; trades a little strength for stability and ductility. | 120 | 165 | 5 | 65 HB | 28 % IACS |
As CastDefault generic Zn-5Al slush casting alloy, no post-cast treatment | Default condition for hollow ornamental slush castings; use as poured after trimming and polishing. | 130 | 180 | 3 | 70 HB | 27 % IACS |
As Cast, ZA-8 (Zn-8Al-1Cu) base metal | Wider freezing range gives better shell control on large hollow parts and noticeably higher strength/hardness. | 200 | 250 | 2 | 90 HB | 27.7 % IACS |
As Cast, ZA-12 (Zn-11Al-1Cu) base metal | Longest freezing range and highest strength of the common slush bases; chosen for large or semi-structural hollow castings. | 210 | 300 | 2 | 95 HB | 28.3 % IACS |
What is Slush Metal Stabilized?
Slush Metal Stabilized is Slush Metal heat treated to Stabilized — pick when the casting must hold close dimensions after machining or plating; trades a little strength for stability and ductility. Slush Metal Stabilized has a yield strength of 120 MPa (17.4 ksi) and a tensile strength of 165 MPa (23.9 ksi) — weaker than 64% of zinc alloy grades. Elongation at break is 5% and the elastic modulus is 85 GPa (12.3 Msi). Slush Metal Stabilized has a density of 6.6 g/cm³ (0.238 lb/in³), lighter than 64% of zinc alloy grades. It melts at 380°C (716 °F). As Cast is the default condition FabDigit quotes; Stabilized is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 85/100, better than 89% of zinc alloy grades
Slush Metal Stabilized properties
Typical room-temperature values for Slush Metal Stabilized; 21 are specific to this condition. Other listed values are Slush Metal reference data and may not represent this condition. Bars are the position among zinc alloy grades.
Physical3
Slush Metal Stabilized has a density of 6.6 g/cm³ (0.238 lb/in³), lighter than 64% of zinc alloy grades. It melts at 380°C (716 °F).
Mechanical16
Slush Metal Stabilized has a yield strength of 120 MPa (17.4 ksi) and a tensile strength of 165 MPa (23.9 ksi) — weaker than 64% of zinc alloy grades. Elongation at break is 5% and the elastic modulus is 85 GPa (12.3 Msi).
Thermal6
Slush Metal Stabilized is rated for continuous service to 100°C (212 °F). It conducts heat at 113 W/m·K (65.3 BTU/hr·ft·°F), better than 57% of zinc alloy grades. Thermal expansion is 27.4 µm/m·K (15.2 µin/in·°F).
Electrical3
Slush Metal Stabilized conducts electricity at 28 % IACS, better than 75% of zinc alloy grades.
Chemical & Environmental3
Corrosion resistance is fair (42/100), better than 71% of zinc alloy grades.
Sustainability4
Producing a kilogram of Slush Metal Stabilized takes about 55 MJ of energy and emits 3.4 kg of CO₂ — more than 71% of zinc alloy grades. Typical recycled content is 45%.
Manufacturability8
Slush Metal Stabilized's machinability is very good (80/100, better than 64% of zinc alloy grades); weldability poor (15/100); formability poor (15/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Slush Metal Stabilized
Is Slush Metal easy to machine?
Cuts very easily with sharp positive-rake carbide or HSS tools at high speed and light feed; thin slush walls need gentle clamping to avoid collapse.
Can Slush Metal be welded?
Effectively unweldable by fusion; join by soft soldering (Zn/Sn-Zn alloys with active flux) or adhesives, or cast integral features.
Can Slush Metal be formed, bent or molded?
Pour at ~430–470 °C into a cool steel or bronze mold, hold seconds to build the shell, then invert to drain the liquid core; wall thickness is set by pour temperature, mold temperature and dwell time.
What surface finishes work on Slush Metal?
Buffs to a bright surface and takes copper/nickel/chromium plating or antique lacquer readily; no anodizing, and chromate/lacquer is recommended for humid or outdoor exposure.
Slush Metal chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Alraised to 8–12 % when ZA-8/ZA-12 base is used for a wider freezing range | 3.5 – 6 | 5 |
| Curaises strength and hardness; too much promotes ageing growth | 0 – 1.5 | 0.5 |
| Mgsuppresses intergranular corrosion from impurities | 0.01 – 0.06 | 0.03 |
| Fe | ≤ 0.1 | 0.03 |
| Pbimpurity limit — critical for long-term dimensional stability | ≤ 0.01 | 0 |
| Cd | ≤ 0 | 0 |
| Sn | ≤ 0 | 0 |
| Zn | balance | — |
Slush Metal Stabilized — frequently asked
What is Slush Metal Stabilized used for?
Slush Metal Stabilized is typically used for decorative castings and ornaments, lamp bases and lighting bodies, figurines, statuettes and trophies, candlesticks and holloware, furniture and cabinet hardware and mirror and clock frames. In short: decorative slush-cast zinc.
What is the yield strength of Slush Metal Stabilized?
Slush Metal Stabilized has a typical yield strength of 120 MPa (17.4 ksi) and a tensile strength of 165 MPa (23.9 ksi) — weaker than 64% of zinc alloy grades. Strength varies by condition: see the 5 listed tempers.
Is Slush Metal Stabilized easy to machine?
Yes — machinability is rated very good (80/100, better than 64% of zinc alloy grades). Cuts very easily with sharp positive-rake carbide or HSS tools at high speed and light feed; thin slush walls need gentle clamping to avoid collapse.
Can Slush Metal Stabilized be welded?
Not readily — weldability is rated poor (15/100). Effectively unweldable by fusion; join by soft soldering (Zn/Sn-Zn alloys with active flux) or adhesives, or cast integral features.
What surface finishes work on Slush Metal Stabilized?
Buffs to a bright surface and takes copper/nickel/chromium plating or antique lacquer readily; no anodizing, and chromate/lacquer is recommended for humid or outdoor exposure.
Can Slush Metal Stabilized be formed, bent or molded?
Pour at ~430–470 °C into a cool steel or bronze mold, hold seconds to build the shell, then invert to drain the liquid core; wall thickness is set by pour temperature, mold temperature and dwell time.
What is the maximum service temperature of Slush Metal Stabilized?
Slush Metal Stabilized is rated for continuous use to about 100°C (212 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASM Handbook Vol.15: Casting — Slush Casting and Zinc Casting Alloys — ASM International (2008)
- ASM Handbook Vol.2: Properties and Selection — Nonferrous Alloys (Zinc and Zinc Alloys) — ASM International (1990)
- ASTM B240 — Zinc and Zinc-Aluminum Alloys in Ingot Form for Castings — ASTM International (2016)
- ASTM B86 — Zinc and Zinc-Aluminum Alloy Foundry and Die Castings — ASTM International (2018)
- ILZRO / Eastern Alloys zinc alloy property data (Zamak 3, ZA-8, ZA-12) — International Lead Zinc Research Organization (2019)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.