Steel P6 CARB-58
Heat-treated state
AISI/SAE P6 · UNS T51606
CARB-58 = carburized, hardened & tempered
Standard service condition: hard wear-resistant case over a tough low-carbon core for impact-loaded mold parts.
Values for the CARB-58 condition
Other P6 tempers and conditions
P6 is listed in 5 conditions; see the grade overview at P6.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Spheroidize annealed | Pick when cavities are to be cold-hobbed with a master punch; softest achievable structure. | 350 | 585 | 25 | 165 HB | 6 % IACS |
ANNDefault Annealed | Standard stock condition for machining or cold hobbing of cavities before carburizing. | 415 | 655 | 20 | 195 HB | — |
Normalized | Used to refine grain and homogenize forged or hobbed blanks before carburizing. | 550 | 830 | 17 | 23 HRC | 5.5 % IACS |
Hardened & tempered | Direct oil quench without carburizing for tough holder/backing parts that need strength but not a wear surface. | 900 | 1,100 | 14 | 35 HRC | — |
CARB-58This page Carburized, hardened & tempered | Standard service condition: hard wear-resistant case over a tough low-carbon core for impact-loaded mold parts. | 930 | 1,150 | 12 | 60 HRC | 32 W/m·K |
What is P6 CARB-58?
P6 CARB-58 is P6 heat treated to CARB-58 — standard service condition: hard wear-resistant case over a tough low-carbon core for impact-loaded mold parts. P6 CARB-58 has a yield strength of 930 MPa (135 ksi) and a tensile strength of 1,150 MPa (167 ksi) — stronger than 90% of steel grades. Elongation at break is 12% and the elastic modulus is 208 GPa (30.2 Msi). P6 CARB-58 has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F). ANN is the default condition FabDigit quotes; CARB-58 is available on request or by drawing note.
Advantages
- High strength — 930 MPa (135 ksi), better than 90% of steel grades
- Polishes to a fine finish — 70/100, better than 87% of steel grades
Limitations
- Difficult to machine — 12/100, worse than 99% of steel grades
- Limited formability — 5/100, worse than 99% of steel grades
- Limited service temperature — 180°C (356 °F), worse than 98% of steel grades
- Low fracture toughness — 30 MPa·√m (27.3 ksi·√in), worse than 96% of steel grades
- Difficult to weld — 15/100, worse than 91% of steel grades
P6 CARB-58 properties
Typical room-temperature values for P6 CARB-58; 18 are specific to this condition. Other listed values are P6 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
P6 CARB-58 has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F).
Mechanical16
P6 CARB-58 has a yield strength of 930 MPa (135 ksi) and a tensile strength of 1,150 MPa (167 ksi) — stronger than 90% of steel grades. Elongation at break is 12% and the elastic modulus is 208 GPa (30.2 Msi).
Thermal6
P6 CARB-58 is rated for continuous service to 180°C (356 °F). It conducts heat at 32 W/m·K (18.5 BTU/hr·ft·°F), worse than 82% of steel grades. Thermal expansion is 11.8 µm/m·K (6.56 µin/in·°F).
Electrical2
P6 CARB-58 has an electrical resistivity of 3×10⁻⁷ Ω·m.
Chemical & Environmental3
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of P6 CARB-58 takes about 34 MJ of energy and emits 2.4 kg of CO₂ — more than 82% of steel grades. Typical recycled content is 45%.
Manufacturability8
P6 CARB-58's machinability is not recommended (12/100, worse than 99% of steel grades); weldability poor (15/100); formability not recommended (5/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with P6 CARB-58
Is P6 easy to machine?
Machine fully in the annealed state with sharp, positive-rake carbide or HSS; the soft, gummy low-carbon Ni-Cr matrix smears, so use high feed, flood coolant and finish before carburizing.
Can P6 be welded?
Weld only annealed or normalized material with a low-carbon/low-alloy filler, preheat 200–300 °C, then re-anneal or re-carburize; welding a carburized case invites cracking.
Can P6 be formed, bent or molded?
Its main advantage is cold hobbing — cavity impressions can be pressed into the soft annealed blank, with stress-relief anneals between hobbing passes.
What surface finishes work on P6?
Case-hardened surfaces polish and texture well after tempering; add hard chrome or electroless nickel for corrosion protection since the steel rusts readily.
P6 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon for cold hobbability | 0.05 – 0.15 | 0.1 |
| Mn | 0.35 – 0.7 | 0.5 |
| Si | 0.1 – 0.4 | 0.25 |
| Cr | 1 – 1.75 | 1.5 |
| Nicore toughness | 3.25 – 3.75 | 3.5 |
| P | ≤ 0.03 | — |
| S | ≤ 0.03 | — |
| Fe | balance | — |
P6 CARB-58 — frequently asked
What is P6 CARB-58 used for?
P6 CARB-58 is typically used for carburized mold cores, impact-resistant mold inserts and die components. In short: hobbable mold steel; tough core, hard case; impact-duty P grade.
What is the yield strength of P6 CARB-58?
P6 CARB-58 has a typical yield strength of 930 MPa (135 ksi) and a tensile strength of 1,150 MPa (167 ksi) — stronger than 90% of steel grades. Strength varies by condition: see the 5 listed tempers.
Is P6 CARB-58 easy to machine?
Not especially — machinability is rated not recommended (12/100, worse than 99% of steel grades). Machine fully in the annealed state with sharp, positive-rake carbide or HSS; the soft, gummy low-carbon Ni-Cr matrix smears, so use high feed, flood coolant and finish before carburizing.
Can P6 CARB-58 be welded?
Not readily — weldability is rated poor (15/100). Weld only annealed or normalized material with a low-carbon/low-alloy filler, preheat 200–300 °C, then re-anneal or re-carburize; welding a carburized case invites cracking.
What surface finishes work on P6 CARB-58?
Case-hardened surfaces polish and texture well after tempering; add hard chrome or electroless nickel for corrosion protection since the steel rusts readily.
Can P6 CARB-58 be formed, bent or molded?
Its main advantage is cold hobbing — cavity impressions can be pressed into the soft annealed blank, with stress-relief anneals between hobbing passes.
What is the maximum service temperature of P6 CARB-58?
P6 CARB-58 is rated for continuous use to about 180°C (356 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between P6-ANN and P6 CARB-58?
ANN is the default condition — standard stock condition for machining or cold hobbing of cavities before carburizing. CARB-58: standard service condition: hard wear-resistant case over a tough low-carbon core for impact-loaded mold parts. Yield strength is 415 MPa in ANN versus 930 MPa in CARB-58.
Sources
- ASTM A681 — Alloy Tool Steels — ASTM International (2015)
- ASM Handbook Vol.1: Properties and Selection: Irons, Steels, and High-Performance Alloys (Tool Steels) — ASM International (1990)
- Tool Steels, 5th ed. (Roberts, Krauss, Kennedy) — ASM International (1998)
- UNS T51606 alloy record — SAE/ASTM Unified Numbering System (2017)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.