Titanium Ti Grade 4 Annealed vs Ti Grade 4 CWSR
Titanium · Ti Grade 4 temper comparison
Ti Grade 4 Annealed and Ti Grade 4 CWSR are two conditions of the same titanium grade, Ti Grade 4: Annealed versus CWSR (cold Worked + Stress Relieved). The chemistry is identical, so every difference below comes from the condition. Ti Grade 4 CWSR is the stronger of the two: yield strength 680 MPa (98.6 ksi) against 520 MPa (75.4 ksi) for Ti Grade 4 Annealed, about 31% more; tensile strength follows at 780 MPa (113 ksi) vs 620 MPa (89.9 ksi). In exchange, Ti Grade 4 Annealed is the more ductile: elongation 20% versus 13% for Ti Grade 4 CWSR, and Ti Grade 4 CWSR is harder (295 HB vs 250 HB). Ti Grade 4 Annealed runs hotter in service (300°C vs 250°C continuous). On the shop floor, Ti Grade 4 Annealed welds better (excellent vs very good).
Ti Grade 4 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Ti Grade 4 CWSRChoose it when strength drives the design.
Ti Grade 4 Annealed vs Ti Grade 4 CWSR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Ti Grade 4 AnnealedTi Grade 4 CWSR
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,660°C3,020 °F · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 17 W/m·K9.8 BTU/hr·ft·°F · Specific Heat Capacity 540 J/kg·K0.13 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Latent Heat of Fusion 295 J/g127 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 40 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 650 MJ/kg279,450 BTU/lb · Embodied Carbon (primary production) 45 kg CO₂/kg · Embodied Water 900 L/kg108 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Ti Grade 4 Annealed vs Ti Grade 4 CWSR — frequently asked
Is Ti Grade 4 CWSR stronger than Ti Grade 4 Annealed?
Yes. Ti Grade 4 CWSR has a typical yield strength of 680 MPa (98.6 ksi) against 520 MPa (75.4 ksi) for Ti Grade 4 Annealed — about 31% more. Tensile strength is 780 MPa (113 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, Annealed or CWSR?
Annealed is the default Ti Grade 4 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Ti Grade 4 Annealed or Ti Grade 4 CWSR?
Ti Grade 4 Annealed. Its weldability rates excellent (85/100) against very good (75/100) for Ti Grade 4 CWSR.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ti Grade 4 Annealed and Ti Grade 4 CWSR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.